FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
NBS Smoke Density, Flaming, Dmax | 225 | - | ASTM E662 |
NBS Smoke Density, Flaming, Ds 1.5 min | 40 | - | ASTM E662 |
NBS Smoke Density, Flaming, Ds 4 min | 150 | - | ASTM E662 |
CYCOLOY CS9610 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend is an injection moldable low smoke, non chlorinated/brominated flame retardant grade. It has good mechanical and impact properties and has a UL94 V0@2.0mm and 5VB@2.0mm flame rating.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
NBS Smoke Density, Flaming, Dmax | 225 | - | ASTM E662 |
NBS Smoke Density, Flaming, Ds 1.5 min | 40 | - | ASTM E662 |
NBS Smoke Density, Flaming, Ds 4 min | 150 | - | ASTM E662 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 800 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 72 | J | ASTM D3763 |
Izod Impact, notched 80*10*3 +23°C | 45 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*3 -30°C | 15 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 45 | kJ/m² | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 15 | kJ/m² | ISO 179/1eA |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 90 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.04 | % | |
Melt Temperature | 270 - 300 | °C | |
Nozzle Temperature | 265 - 300 | °C | |
Front - Zone 3 Temperature | 265 - 300 | °C | |
Middle - Zone 2 Temperature | 260 - 300 | °C | |
Rear - Zone 1 Temperature | 260 - 300 | °C | |
Hopper Temperature | 60 - 80 | °C | |
Mold Temperature | 60 - 90 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 40 - 70 | rpm | |
Shot to Cylinder Size | 40 - 80 | % | |
Vent Depth | 0.038 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 64 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 62 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 55 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 2600 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 98 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2440 | MPa | ASTM D790 |
Tensile Stress, yield, 50 mm/min | 62 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 50 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 4.8 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | >45 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2400 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 98 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2500 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.2 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.6 | % | SABIC method |
Melt Flow Rate, 260°C/5.0 kgf | 15 | g/10 min | ASTM D1238 |
Melt Volume Rate, MVR at 260°C/5.0 kg | 12 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 118 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 105 | °C | ASTM D648 |
Vicat Softening Temp, Rate B/50 | 124 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 127 | °C | ISO 306 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 106 | °C | ISO 75/Af |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94-5VB Flame Class Rating | ≥2 | mm | UL 94 |
UL Recognized, 94V-0 Flame Class Rating | 2 | mm | UL 94 |
NBS Smoke Density, Flaming, Dmax | 225 | - | ASTM E662 |
NBS Smoke Density, Flaming, Ds 1.5 min | 40 | - | ASTM E662 |
NBS Smoke Density, Flaming, Ds 4 min | 150 | - | ASTM E662 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 800 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 72 | J | ASTM D3763 |
Izod Impact, notched 80*10*3 +23°C | 45 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*3 -30°C | 15 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 45 | kJ/m² | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 15 | kJ/m² | ISO 179/1eA |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 90 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.04 | % | |
Melt Temperature | 270 - 300 | °C | |
Nozzle Temperature | 265 - 300 | °C | |
Front - Zone 3 Temperature | 265 - 300 | °C | |
Middle - Zone 2 Temperature | 260 - 300 | °C | |
Rear - Zone 1 Temperature | 260 - 300 | °C | |
Hopper Temperature | 60 - 80 | °C | |
Mold Temperature | 60 - 90 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 40 - 70 | rpm | |
Shot to Cylinder Size | 40 - 80 | % | |
Vent Depth | 0.038 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 64 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 62 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 55 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 2600 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 98 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2440 | MPa | ASTM D790 |
Tensile Stress, yield, 50 mm/min | 62 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 50 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 4.8 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | >45 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2400 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 98 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2500 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.2 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.6 | % | SABIC method |
Melt Flow Rate, 260°C/5.0 kgf | 15 | g/10 min | ASTM D1238 |
Melt Volume Rate, MVR at 260°C/5.0 kg | 12 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 118 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 105 | °C | ASTM D648 |
Vicat Softening Temp, Rate B/50 | 124 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 127 | °C | ISO 306 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 106 | °C | ISO 75/Af |
Relative Temp Index, Elec | 90 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 90 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 90 | °C | UL 746B |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
NBS Smoke Density, Flaming, Dmax | 225 | - | ASTM E662 |
NBS Smoke Density, Flaming, Ds 1.5 min | 40 | - | ASTM E662 |
NBS Smoke Density, Flaming, Ds 4 min | 150 | - | ASTM E662 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 800 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 72 | J | ASTM D3763 |
Izod Impact, notched 80*10*3 +23°C | 45 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*3 -30°C | 15 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 45 | kJ/m² | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 15 | kJ/m² | ISO 179/1eA |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 90 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.04 | % | |
Melt Temperature | 270 - 300 | °C | |
Nozzle Temperature | 265 - 300 | °C | |
Front - Zone 3 Temperature | 265 - 300 | °C | |
Middle - Zone 2 Temperature | 260 - 300 | °C | |
Rear - Zone 1 Temperature | 260 - 300 | °C | |
Hopper Temperature | 60 - 80 | °C | |
Mold Temperature | 60 - 90 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 40 - 70 | rpm | |
Shot to Cylinder Size | 40 - 80 | % | |
Vent Depth | 0.038 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 64 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 62 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 55 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 2600 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 98 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2440 | MPa | ASTM D790 |
Tensile Stress, yield, 50 mm/min | 62 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 50 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 4.8 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | >45 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2400 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 98 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2500 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.2 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.6 | % | SABIC method |
Melt Flow Rate, 260°C/5.0 kgf | 15 | g/10 min | ASTM D1238 |
Melt Volume Rate, MVR at 260°C/5.0 kg | 12 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 118 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 105 | °C | ASTM D648 |
Vicat Softening Temp, Rate B/50 | 124 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 127 | °C | ISO 306 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 106 | °C | ISO 75/Af |