PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Hot-Wire Ignition (HWI), PLC 2 | ≥3 | mm | UL 746A |
CYCOLOY RCM6134 resin is an injection moldable filled PC/ABS blend with non-brominated and non-chlorinated flame retardant. It contains 35% post consumer recycle content with a UL-94 V0 rating @ 1.0mm. Developed for thin wall applications that require high flow and high stiffness performance. Limited availability and restricted color only.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Hot-Wire Ignition (HWI), PLC 2 | ≥3 | mm | UL 746A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | ≥1 | mm | UL 94 |
UL Recognized, 94V-1 Flame Class Rating | ≥0.8 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 300 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 52 | J | ASTM D3763 |
Izod Impact, notched 80*10*3 +23°C | 20 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 11 | kJ/m² | ISO 179/1eA |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 - 90 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 8 | Hrs | |
Maximum Moisture Content | 0.04 | % | |
Melt Temperature | 245 - 275 | °C | |
Nozzle Temperature | 245 - 275 | °C | |
Front - Zone 3 Temperature | 245 - 275 | °C | |
Middle - Zone 2 Temperature | 220 - 265 | °C | |
Rear - Zone 1 Temperature | 220 - 255 | °C | |
Mold Temperature | 60 - 80 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 40 - 70 | rpm | |
Shot to Cylinder Size | 30 - 80 | % | |
Vent Depth | 0.038 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 5 mm/min | 54 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min | 44 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 5 mm/min | 3.5 | % | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 70 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 3100 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 90 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 3100 | MPa | ASTM D790 |
Tensile Stress, yield, 5 mm/min | 56 | MPa | ISO 527 |
Tensile Stress, break, 5 mm/min | 48 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min | 3.4 | % | ISO 527 |
Tensile Strain, break, 5 mm/min | 75 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 3100 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 95 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 3100 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.22 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.3 - 0.5 | % | SABIC method |
Mold Shrinkage, xflow, 3.2 mm | 0.3 - 0.5 | % | SABIC method |
Melt Flow Rate, 260°C/2.16 kgf | 11 | g/10 min | ASTM D1238 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 88 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 80 | °C | ASTM D648 |
CTE, 23°C to 80°C, flow | 7.E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 81 | °C | ISO 75/Af |
Relative Temp Index, Elec | 60 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 60 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature