ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Hot-Wire Ignition (HWI), PLC 2 | ≥3 | mm | UL 746A |
CYCOLOY* RCX7243 is an impact modified PC blend containing 30% PCR content with non-brominated and non-chlorinated FR for thin-wall applications requiring excellent impact/flow balance performance.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Hot-Wire Ignition (HWI), PLC 2 | ≥3 | mm | UL 746A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | ≥0.75 | mm | UL 94 |
UL Recognized, 94V-1 Flame Class Rating | ≥0.6 | mm | UL 94 |
UL Recognized, 94V-2 Flame Class Rating | ≥0.4 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 690 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 130 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 57 | J | ASTM D3763 |
Izod Impact, notched 80*10*3 +23°C | 50 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 - 90 | °C | |
Drying Time | 2 - 4 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 250 - 300 | °C | |
Nozzle Temperature | 250 - 300 | °C | |
Front - Zone 3 Temperature | 250 - 300 | °C | |
Middle - Zone 2 Temperature | 240 - 290 | °C | |
Rear - Zone 1 Temperature | 230 - 280 | °C | |
Hopper Temperature | 60 - 80 | °C | |
Mold Temperature | 60 - 85 | °C | |
Vent Depth | 0.03 - 0.075 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 58 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 53 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 4 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 60 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 2400 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 100 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2350 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.19 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.6 | % | SABIC method |
Melt Flow Rate, 260°C/2.16 kgf | 19 | g/10 min | ASTM D1238 |
Water Absorption, (23°C/saturated) | 0.15 | % | ISO 62-1 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 104 | °C | ASTM D1525 |
HDT, 1.82 MPa, 3.2mm, unannealed | 86 | °C | ASTM D648 |
HDT, 0.45 MPa, 6.4 mm, unannealed | 101 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 7.5E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 7.5E-05 | 1/°C | ASTM E831 |
Relative Temp Index, Elec | 80 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.