Tensile Stress, yld, Type I, 50 mm/min |
50 |
MPa |
ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min |
45 |
MPa |
ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min |
5 |
% |
ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min |
>50 |
% |
ASTM D638 |
Tensile Modulus, 5 mm/min |
2400 |
MPa |
ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span |
75 |
MPa |
ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span |
2300 |
MPa |
ASTM D790 |
Taber Abrasion, CS-17, 1 kg |
70 |
mg/1000cy |
SABIC method |
Tensile Stress, yield, 5 mm/min |
44 |
MPa |
ISO 527 |
Tensile Stress, break, 5 mm/min |
44 |
MPa |
ISO 527 |
Tensile Stress, yield, 50 mm/min |
48 |
MPa |
ISO 527 |
Tensile Stress, break, 50 mm/min |
44 |
MPa |
ISO 527 |
Tensile Strain, yield, 5 mm/min |
5 |
% |
ISO 527 |
Tensile Strain, break, 5 mm/min |
>50 |
% |
ISO 527 |
Tensile Strain, yield, 50 mm/min |
5 |
% |
ISO 527 |
Tensile Strain, break, 50 mm/min |
>50 |
% |
ISO 527 |
Tensile Modulus, 1 mm/min |
2400 |
MPa |
ISO 527 |
Flexural Stress, yield, 2 mm/min |
75 |
MPa |
ISO 178 |
Flexural Modulus, 2 mm/min |
2300 |
MPa |
ISO 178 |
Hardness, Rockwell L |
90 |
- |
ISO 2039-2 |
Hardness, Rockwell R |
115 |
- |
ISO 2039-2 |