FLEX NORYL WCD795 resin is a flexible, non-reinforced extrudable blend of Polyphenylene Ether (PPE) + Thermoplastic Elastomer (TPE). This material contains non-halogenated flame retardant and performance capable of meeting UL 1581 VW-1 requirements. FLEX NORYL WCD795 resin is intended for evaluation in AC cable jacket applications that require UL62 SVE and NISPE configurations at 90C or 105C temperature rating and black color. It has a Shore A Hardness reading of 79 and exhibits superior thermal stability, very low water absorption, good electric properties, and low specific gravity. Processing is typically conducted on standard extrusion equipment, and UL 1581 testing is conducted on 2.0mm wire with 0.12mm X 20 stranded copper conductor.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Volume Resistivity | 1.4E+16 | Ω.cm | ASTM D257 |
| Relative Permittivity, 1 MHz | 2.6 | - | ASTM D150 |
| Dissipation Factor, 1 MHz | 0.007 | - | ASTM D150 |
| Dielectric strength in oil, 2.0mm | 24.5 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Smoke Density on 0.5mm plaque, Non-flame, Ds, max | 70 | - | ASTM E662 |
| Smoke Density on 0.5mm plaque, Flame, Ds, max | 117 | - | ASTM E662 |
| Glow Wire Flammability Index 960°C, passes at | 3 | mm | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature, 3.0 mm | 800 | °C | IEC 60695-2-13 |
| Oxygen Index (LOI) | 27 | % | ISO 4589 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Brittleness Temperature | <-40 | °C | ASTM D746 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 50 mm/min | 14 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 240 | % | ASTM D638 |
| Flexural Modulus, 12.5 mm/min, 100 mm span | 30 | MPa | ASTM D790 |
| Hardness, Shore A, 30S reading | 79 | - | ASTM D2240 |
| Tensile Stress, break, 50 mm/min | 14 | MPa | ISO 527 |
| Tensile Strain, break, 50 mm/min | 215 | % | ISO 527 |
| Flexural Modulus, 12.5 mm/min | 30 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.02 | - | ASTM D792 |
| Melt Flow Rate, 250°C/10.0 kgf | 11 | g/10 min | ASTM D1238 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile strength @ break | 23 | MPa | UL 1581 |
| Tensile elongation @ break | 310 | % | UL 1581 |
| Tensile strength @ break after 7days @136°C | 21 | MPa | UL 1581 |
| Tensile elongation @ break after 7days @136°C | 246 | % | UL 1581 |
| Heat Deformation at 121°C/250g | 8 | % | UL 1581 |
| VW-1 | Pass | - | UL 1581 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 75 - 85 | °C | |
| Drying Time | 5 - 7 | Hrs | |
| Drying Time (Cumulative) | 12 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Extruder Length/Diameter Ratio (L/D) | 22:1 to 26:1 | - | |
| Screw Speed | 15 - 85 | rpm | |
| Feed Zone Temperature | 180 - 220 | °C | |
| Middle Zone Temperatures | 220 - 250 | °C | |
| Head Zone Temperature | 220 - 250 | °C | |
| Neck Temperature | 220 - 250 | °C | |
| Cross-head Temperature | 220 - 250 | °C | |
| Die Temperature | 220 - 250 | °C | |
| Melt Temperature | 220 - 250 | °C | |
| Conductor Pre-heat Temperature | 25 - 120 | °C | |
| Screen Pack | 150 - 100 | - | |
| Cooling Water Air Gap | 100 - 200 | mm | |
| Water Bath Temperature | 15 - 60 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Volume Resistivity | 1.4E+16 | Ω.cm | ASTM D257 |
| Relative Permittivity, 1 MHz | 2.6 | - | ASTM D150 |
| Dissipation Factor, 1 MHz | 0.007 | - | ASTM D150 |
| Dielectric strength in oil, 2.0mm | 24.5 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Smoke Density on 0.5mm plaque, Non-flame, Ds, max | 70 | - | ASTM E662 |
| Smoke Density on 0.5mm plaque, Flame, Ds, max | 117 | - | ASTM E662 |
| Glow Wire Flammability Index 960°C, passes at | 3 | mm | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature, 3.0 mm | 800 | °C | IEC 60695-2-13 |
| Oxygen Index (LOI) | 27 | % | ISO 4589 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Brittleness Temperature | <-40 | °C | ASTM D746 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 50 mm/min | 14 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 240 | % | ASTM D638 |
| Flexural Modulus, 12.5 mm/min, 100 mm span | 30 | MPa | ASTM D790 |
| Hardness, Shore A, 30S reading | 79 | - | ASTM D2240 |
| Tensile Stress, break, 50 mm/min | 14 | MPa | ISO 527 |
| Tensile Strain, break, 50 mm/min | 215 | % | ISO 527 |
| Flexural Modulus, 12.5 mm/min | 30 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.02 | - | ASTM D792 |
| Melt Flow Rate, 250°C/10.0 kgf | 11 | g/10 min | ASTM D1238 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile strength @ break | 23 | MPa | UL 1581 |
| Tensile elongation @ break | 310 | % | UL 1581 |
| Tensile strength @ break after 7days @136°C | 21 | MPa | UL 1581 |
| Tensile elongation @ break after 7days @136°C | 246 | % | UL 1581 |
| Heat Deformation at 121°C/250g | 8 | % | UL 1581 |
| VW-1 | Pass | - | UL 1581 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 75 - 85 | °C | |
| Drying Time | 5 - 7 | Hrs | |
| Drying Time (Cumulative) | 12 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Extruder Length/Diameter Ratio (L/D) | 22:1 to 26:1 | - | |
| Screw Speed | 15 - 85 | rpm | |
| Feed Zone Temperature | 180 - 220 | °C | |
| Middle Zone Temperatures | 220 - 250 | °C | |
| Head Zone Temperature | 220 - 250 | °C | |
| Neck Temperature | 220 - 250 | °C | |
| Cross-head Temperature | 220 - 250 | °C | |
| Die Temperature | 220 - 250 | °C | |
| Melt Temperature | 220 - 250 | °C | |
| Conductor Pre-heat Temperature | 25 - 120 | °C | |
| Screen Pack | 150 - 100 | - | |
| Cooling Water Air Gap | 100 - 200 | mm | |
| Water Bath Temperature | 15 - 60 | °C |