High heat polycarbonate copolymer blend with an excellent balance of heat resistance, processability, and impact strength. Available in a range of opaque colors.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 639 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 331 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 75 | J | ASTM D3763 |
| Instrumented Dart Impact Total Energy, -30°C | 78 | J | ASTM D3763 |
| Izod Impact, notched 80*10*4 +23°C | 43 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 20 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 48 | kJ/m² | ISO 179/1eA |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 48 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 310 - 330 | °C | |
| Nozzle Temperature | 305 - 325 | °C | |
| Front - Zone 3 Temperature | 310 - 330 | °C | |
| Middle - Zone 2 Temperature | 300 - 320 | °C | |
| Rear - Zone 1 Temperature | 290 - 310 | °C | |
| Mold Temperature | 80 - 115 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Shot to Cylinder Size | 40 - 60 | % | |
| Vent Depth | 0.025 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 50 mm/min | 64 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 63 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 6.7 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 102 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2180 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 101 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2230 | MPa | ASTM D790 |
| Tensile Stress, yield, 50 mm/min | 62 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 59 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6.6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 96.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2160 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/min | 2040 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.2 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.6 - 0.8 | % | SABIC method |
| Melt Flow Rate, 300°C/1.2 kgf | 5.6 | g/10 min | ASTM D1238 |
| Density | 1.1 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.24 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.09 | % | ISO 62 |
| Melt Volume Rate, MVR at 330°C/2.16kg | 31 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Vicat Softening Temp, Rate B/50 | 156 | °C | ASTM D1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 136 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 6.16E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 6.73E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 6.16E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 6.73E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 155 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 157 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 134 | °C | ISO 75/Af |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.