ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | >1.E+15 | Ω.cm | ASTM D257 |
Surface Resistivity | >1.E+15 | Ω | ASTM D257 |
LEXAN EXL1494T polycarbonate (PC) siloxane copolymer resin is an injection molding grade with FDA and EU food contact compliance. This resin offers extreme low temperature (-40 C) ductility in combination with medium flow characteristics, improved release and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL1494T resin is available in transparent and opaque colors and is an excellent candidate for a broad range of food contact applications.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | >1.E+15 | Ω.cm | ASTM D257 |
Surface Resistivity | >1.E+15 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-2 Flame Class Rating | ≥3 | mm | UL 94 |
Glow Wire Ignitability Temperature, 3.0 mm | 850 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature, 2.5 mm | 850 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature, 1.5 mm | 850 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature, 0.8 mm | 850 | °C | IEC 60695-2-13 |
Glow Wire Flammability Index, 3.0 mm | 960 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index, 2.5 mm | 825 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index, 1.5 mm | 825 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index, 0.8 mm | 825 | °C | IEC 60695-2-12 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 824 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 712 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 75 | J | ASTM D3763 |
Instrumented Dart Impact Total Energy, -30°C | 77 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*3 +23°C | 65 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*3 -30°C | 55 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 70 | kJ/m² | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 60 | kJ/m² | ISO 179/1eA |
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 48 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 295 - 315 | °C | |
Nozzle Temperature | 290 - 310 | °C | |
Front - Zone 3 Temperature | 295 - 315 | °C | |
Middle - Zone 2 Temperature | 280 - 305 | °C | |
Rear - Zone 1 Temperature | 270 - 295 | °C | |
Mold Temperature | 70 - 95 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 40 - 70 | rpm | |
Shot to Cylinder Size | 40 - 60 | % | |
Vent Depth | 0.025 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 57 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 59 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 5.6 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 123.9 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 2180 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 92 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2180 | MPa | ASTM D790 |
Hardness, Rockwell L | 87 | - | ASTM D785 |
Tensile Stress, yield, 50 mm/min | 56 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 55 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 5.4 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 108.5 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2300 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 88 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2120 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Light Transmission, 2.54 mm | 82 | % | ASTM D1003 |
Haze, 2.54 mm | 3 | % | ASTM D1003 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.19 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.8 | % | SABIC method |
Mold Shrinkage, xflow, 3.2 mm | 0.4 - 0.8 | % | SABIC method |
Melt Flow Rate, 300°C/1.2 kgf | 10 | g/10 min | ASTM D1238 |
Density | 1.19 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 0.12 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.09 | % | ISO 62 |
Melt Volume Rate, MVR at 300°C/1.2 kg | 9 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate A/50 | 138 | °C | ASTM D1525 |
HDT, 1.82 MPa, 3.2mm, unannealed | 120 | °C | ASTM D648 |
CTE, -40°C to 95°C, flow | 6.7E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 95°C, xflow | 8.E-05 | 1/°C | ASTM E831 |
CTE, 23°C to 80°C, flow | 6.7E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | pass | - | IEC 60695-10-2 |
Vicat Softening Temp, Rate B/50 | 138 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 139 | °C | ISO 306 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 116 | °C | ISO 75/Af |
Relative Temp Index, Elec | 130 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 120 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 130 | °C | UL 746B |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | >1.E+15 | Ω.cm | ASTM D257 |
Surface Resistivity | >1.E+15 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-2 Flame Class Rating | ≥3 | mm | UL 94 |
Glow Wire Ignitability Temperature, 3.0 mm | 850 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature, 2.5 mm | 850 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature, 1.5 mm | 850 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature, 0.8 mm | 850 | °C | IEC 60695-2-13 |
Glow Wire Flammability Index, 3.0 mm | 960 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index, 2.5 mm | 825 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index, 1.5 mm | 825 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index, 0.8 mm | 825 | °C | IEC 60695-2-12 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 824 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 712 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 75 | J | ASTM D3763 |
Instrumented Dart Impact Total Energy, -30°C | 77 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*3 +23°C | 65 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*3 -30°C | 55 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 70 | kJ/m² | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 60 | kJ/m² | ISO 179/1eA |
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 48 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 295 - 315 | °C | |
Nozzle Temperature | 290 - 310 | °C | |
Front - Zone 3 Temperature | 295 - 315 | °C | |
Middle - Zone 2 Temperature | 280 - 305 | °C | |
Rear - Zone 1 Temperature | 270 - 295 | °C | |
Mold Temperature | 70 - 95 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 40 - 70 | rpm | |
Shot to Cylinder Size | 40 - 60 | % | |
Vent Depth | 0.025 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 57 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 59 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 5.6 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 123.9 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 2180 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 92 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2180 | MPa | ASTM D790 |
Hardness, Rockwell L | 87 | - | ASTM D785 |
Tensile Stress, yield, 50 mm/min | 56 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 55 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 5.4 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 108.5 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2300 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 88 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2120 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Light Transmission, 2.54 mm | 82 | % | ASTM D1003 |
Haze, 2.54 mm | 3 | % | ASTM D1003 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.19 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.8 | % | SABIC method |
Mold Shrinkage, xflow, 3.2 mm | 0.4 - 0.8 | % | SABIC method |
Melt Flow Rate, 300°C/1.2 kgf | 10 | g/10 min | ASTM D1238 |
Density | 1.19 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 0.12 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.09 | % | ISO 62 |
Melt Volume Rate, MVR at 300°C/1.2 kg | 9 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate A/50 | 138 | °C | ASTM D1525 |
HDT, 1.82 MPa, 3.2mm, unannealed | 120 | °C | ASTM D648 |
CTE, -40°C to 95°C, flow | 6.7E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 95°C, xflow | 8.E-05 | 1/°C | ASTM E831 |
CTE, 23°C to 80°C, flow | 6.7E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | pass | - | IEC 60695-10-2 |
Vicat Softening Temp, Rate B/50 | 138 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 139 | °C | ISO 306 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 116 | °C | ISO 75/Af |
Relative Temp Index, Elec | 130 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 120 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 130 | °C | UL 746B |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | >1.E+15 | Ω.cm | ASTM D257 |
Surface Resistivity | >1.E+15 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-2 Flame Class Rating | ≥3 | mm | UL 94 |
Glow Wire Ignitability Temperature, 3.0 mm | 850 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature, 2.5 mm | 850 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature, 1.5 mm | 850 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature, 0.8 mm | 850 | °C | IEC 60695-2-13 |
Glow Wire Flammability Index, 3.0 mm | 960 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index, 2.5 mm | 825 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index, 1.5 mm | 825 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index, 0.8 mm | 825 | °C | IEC 60695-2-12 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 824 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 712 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 75 | J | ASTM D3763 |
Instrumented Dart Impact Total Energy, -30°C | 77 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*3 +23°C | 65 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*3 -30°C | 55 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 70 | kJ/m² | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 60 | kJ/m² | ISO 179/1eA |
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 48 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 295 - 315 | °C | |
Nozzle Temperature | 290 - 310 | °C | |
Front - Zone 3 Temperature | 295 - 315 | °C | |
Middle - Zone 2 Temperature | 280 - 305 | °C | |
Rear - Zone 1 Temperature | 270 - 295 | °C | |
Mold Temperature | 70 - 95 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 40 - 70 | rpm | |
Shot to Cylinder Size | 40 - 60 | % | |
Vent Depth | 0.025 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 57 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 59 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 5.6 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 123.9 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 2180 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 92 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2180 | MPa | ASTM D790 |
Hardness, Rockwell L | 87 | - | ASTM D785 |
Tensile Stress, yield, 50 mm/min | 56 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 55 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 5.4 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 108.5 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2300 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 88 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2120 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Light Transmission, 2.54 mm | 82 | % | ASTM D1003 |
Haze, 2.54 mm | 3 | % | ASTM D1003 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.19 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.8 | % | SABIC method |
Mold Shrinkage, xflow, 3.2 mm | 0.4 - 0.8 | % | SABIC method |
Melt Flow Rate, 300°C/1.2 kgf | 10 | g/10 min | ASTM D1238 |
Density | 1.19 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 0.12 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.09 | % | ISO 62 |
Melt Volume Rate, MVR at 300°C/1.2 kg | 9 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate A/50 | 138 | °C | ASTM D1525 |
HDT, 1.82 MPa, 3.2mm, unannealed | 120 | °C | ASTM D648 |
CTE, -40°C to 95°C, flow | 6.7E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 95°C, xflow | 8.E-05 | 1/°C | ASTM E831 |
CTE, 23°C to 80°C, flow | 6.7E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | pass | - | IEC 60695-10-2 |
Vicat Softening Temp, Rate B/50 | 138 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 139 | °C | ISO 306 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 116 | °C | ISO 75/Af |
Relative Temp Index, Elec | 130 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 120 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 130 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature