LEXAN™ Copolymer EXL9111

LEXAN EXL9111 polycarbonate-Siloxane copolymer resin is a high flow, high impact,non-chlorinated, non-brominated flame retardant opaque injection molding (IM) grade.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Asia

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Flame Retardant
High Flow
Impact resistant
Low temperature impact
Non Cl/Br flame retardant
Non halogenated flame retardant

Industry

Material previously used in

Commercial Appliance
Defense
Electrical
General Healthcare
Material Handling
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Electronic Components
Electronics
Enclosures
Industrial Material Handling
Monitoring and Imaging
Power Manangement
Wireless Communications
Wiring Devices

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	>1E+16	Ω.cm	ASTM D257
Surface Resistivity	>1E+16	Ω	ASTM D257
Dielectric Constant, 1.1 GHz	2.83	-	SABIC method
Dissipation Factor, 1.1 GHz	0.0061	-	SABIC method

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	1.2	mm	UL 94
UL Recognized, 94V-1 Flame Class Rating	≥0.8	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	753	J/m	ASTM D256
Izod Impact, notched, -30°C	124	J/m	ASTM D256
Izod Impact, unnotched, 23°C	NB	J/m	ASTM D4812
Instrumented Dart Impact Total Energy, 23°C	62.5	J	ASTM D3763
Instrumented Dart Impact Total Energy, -30°C	62.3	J	ASTM D3763
*Izod Impact, notched 80104 +23°C*	51.3	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	104	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	NB	kJ/m²	ISO 180/1U
Charpy Impact, notched, 23°C	55.6	kJ/m²	ISO 179/2C
Charpy Impact, notched, -30°C	12.9	kJ/m²	ISO 179/2C
Charpy Impact, unnotched, 23°C	NB	kJ/m²	ISO 179/2C

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100	°C
Drying Time	3 - 4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	280 - 305	°C
Nozzle Temperature	275 - 300	°C
Front - Zone 3 Temperature	280 - 305	°C
Middle - Zone 2 Temperature	275 - 295	°C
Rear - Zone 1 Temperature	260 - 285	°C
Mold Temperature	60 - 80	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Hardness, Rockwell L	92.2	-	ASTM D785
Tensile Stress, yld, Type I, 50 mm/min	60	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	54	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	4.6	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	76.4	%	ASTM D638
Tensile Modulus, 50 mm/min	2387	MPa	ASTM D638
Tensile Stress, yield	60	MPa	ISO 527
Tensile Stress, break	47	MPa	ISO 527
Tensile Strain, break	46.7	%	ISO 527
Tensile Strain, yield	4.5	%	ISO 527
Tensile Modulus, 1 mm/min	2347	MPa	ISO 527
Flexural Stress, yld, 1.3 mm/min, 50 mm span	96.7	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2440	MPa	ASTM D790
Flexural Stress, break, 2 mm/min	93	MPa	ISO 178
Flexural Stress, brk, 1.3 mm/min, 50 mm span	95	MPa	ASTM D790
Flexural Modulus, 2 mm/min	2314	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.19	-	ASTM D792
Density	1.18	g/cm³	ASTM D792
Mold Shrinkage, flow, 24 hrs	0.6	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.62	%	ASTM D955
Melt Flow Rate, 300°C/1.2 kgf	20	g/10 min	ASTM D1238
Moisture Absorption (23°C / 50% RH)	0.43	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	101	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	111	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	103	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	112	°C	ISO 75/Bf
Vicat Softening Temp, Rate B/50	126	°C	ASTM D1525
Vicat Softening Temp, Rate B/50	117	°C	ISO 306
Vicat Softening Temp, Rate B/120	119	°C	ISO 306
CTE, -40°C to 40°C, flow	6.5E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	6.6E-05	1/°C	ASTM E831
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B

THIS SITE USES COOKIES

LEXAN™ Copolymer EXL9111

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

Curve Data

CAE Cards

Register for High value Multi-Point Data

THIS SITE USES COOKIES

LEXAN™ Copolymer EXL9111

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

Curve Data

CAE Cards

Related Documents

Technical Data Sheets

Register for High value Multi-Point Data