FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | ≥0.5 | mm | UL 94 |
55 MFR LEXAN High Flow Ductile Copolymer
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | ≥0.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 674 | J/m | ASTM D256 |
Izod Impact, notched, 0°C | 325 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 108 | J/m | ASTM D256 |
Multiaxial Impact | 92 | J | ISO 6603 |
Instrumented Dart Impact Total Energy, 23°C | 56 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*3 +23°C | 55 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*3 -30°C | 10 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 60 | kJ/m² | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 11 | kJ/m² | ISO 179/1eA |
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 105 - 110 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 24 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 260 - 305 | °C | |
Nozzle Temperature | 255 - 300 | °C | |
Front - Zone 3 Temperature | 260 - 305 | °C | |
Middle - Zone 2 Temperature | 250 - 295 | °C | |
Rear - Zone 1 Temperature | 240 - 280 | °C | |
Mold Temperature | 50 - 80 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 35 - 75 | rpm | |
Shot to Cylinder Size | 40 - 60 | % | |
Vent Depth | 0.038 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 60 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 57 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 5.5 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 114 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 2300 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 100 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2280 | MPa | ASTM D790 |
Hardness, Rockwell R | 120 | - | ASTM D785 |
Tensile Stress, yield, 50 mm/min | 61 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 56 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 100 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2200 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2200 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Light Transmission, 2.54 mm | 88 | % | ASTM D1003 |
Haze, 2.54 mm | <1 | % | ASTM D1003 |
Refractive Index | 1.582 | - | ASTM D542 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.2 | - | ASTM D792 |
Density | 1.2 | g/cm³ | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
Melt Flow Rate, 300°C/1.2 kgf | 55 | g/10 min | ASTM D1238 |
Density | 1.2 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 0.3 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 |
Melt Volume Rate, MVR at 300°C/1.2 kg | 51 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 141 | °C | ASTM D1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed | 124 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 110 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 8.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 8.E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | PASS | - | IEC 60695-10-2 |
Vicat Softening Temp, Rate B/50 | 135 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 136 | °C | ISO 306 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 120 | °C | ISO 75/Af |
Relative Temp Index, Elec | 115 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 115 | °C | UL 746B |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | ≥0.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 674 | J/m | ASTM D256 |
Izod Impact, notched, 0°C | 325 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 108 | J/m | ASTM D256 |
Multiaxial Impact | 92 | J | ISO 6603 |
Instrumented Dart Impact Total Energy, 23°C | 56 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*3 +23°C | 55 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*3 -30°C | 10 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 60 | kJ/m² | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 11 | kJ/m² | ISO 179/1eA |
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 105 - 110 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 24 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 260 - 305 | °C | |
Nozzle Temperature | 255 - 300 | °C | |
Front - Zone 3 Temperature | 260 - 305 | °C | |
Middle - Zone 2 Temperature | 250 - 295 | °C | |
Rear - Zone 1 Temperature | 240 - 280 | °C | |
Mold Temperature | 50 - 80 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 35 - 75 | rpm | |
Shot to Cylinder Size | 40 - 60 | % | |
Vent Depth | 0.038 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 60 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 57 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 5.5 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 114 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 2300 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 100 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2280 | MPa | ASTM D790 |
Hardness, Rockwell R | 120 | - | ASTM D785 |
Tensile Stress, yield, 50 mm/min | 61 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 56 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 100 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2200 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2200 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Light Transmission, 2.54 mm | 88 | % | ASTM D1003 |
Haze, 2.54 mm | <1 | % | ASTM D1003 |
Refractive Index | 1.582 | - | ASTM D542 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.2 | - | ASTM D792 |
Density | 1.2 | g/cm³ | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
Melt Flow Rate, 300°C/1.2 kgf | 55 | g/10 min | ASTM D1238 |
Density | 1.2 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 0.3 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 |
Melt Volume Rate, MVR at 300°C/1.2 kg | 51 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 141 | °C | ASTM D1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed | 124 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 110 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 8.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 8.E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | PASS | - | IEC 60695-10-2 |
Vicat Softening Temp, Rate B/50 | 135 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 136 | °C | ISO 306 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 120 | °C | ISO 75/Af |
Relative Temp Index, Elec | 115 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 115 | °C | UL 746B |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | ≥0.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 674 | J/m | ASTM D256 |
Izod Impact, notched, 0°C | 325 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 108 | J/m | ASTM D256 |
Multiaxial Impact | 92 | J | ISO 6603 |
Instrumented Dart Impact Total Energy, 23°C | 56 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*3 +23°C | 55 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*3 -30°C | 10 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 60 | kJ/m² | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 11 | kJ/m² | ISO 179/1eA |
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 105 - 110 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 24 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 260 - 305 | °C | |
Nozzle Temperature | 255 - 300 | °C | |
Front - Zone 3 Temperature | 260 - 305 | °C | |
Middle - Zone 2 Temperature | 250 - 295 | °C | |
Rear - Zone 1 Temperature | 240 - 280 | °C | |
Mold Temperature | 50 - 80 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 35 - 75 | rpm | |
Shot to Cylinder Size | 40 - 60 | % | |
Vent Depth | 0.038 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 60 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 57 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 5.5 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 114 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 2300 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 100 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2280 | MPa | ASTM D790 |
Hardness, Rockwell R | 120 | - | ASTM D785 |
Tensile Stress, yield, 50 mm/min | 61 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 56 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 100 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2200 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2200 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Light Transmission, 2.54 mm | 88 | % | ASTM D1003 |
Haze, 2.54 mm | <1 | % | ASTM D1003 |
Refractive Index | 1.582 | - | ASTM D542 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.2 | - | ASTM D792 |
Density | 1.2 | g/cm³ | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
Melt Flow Rate, 300°C/1.2 kgf | 55 | g/10 min | ASTM D1238 |
Density | 1.2 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 0.3 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 |
Melt Volume Rate, MVR at 300°C/1.2 kg | 51 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 141 | °C | ASTM D1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed | 124 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 110 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 8.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 8.E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | PASS | - | IEC 60695-10-2 |
Vicat Softening Temp, Rate B/50 | 135 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 136 | °C | ISO 306 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 120 | °C | ISO 75/Af |
Relative Temp Index, Elec | 115 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 115 | °C | UL 746B |