ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Dielectric Strength, in oil, 3.2 mm | 26.5 | kV/mm | ASTM D149 |
Volume Resistivity | >1.E+15 | Ω.cm | IEC 60093 |
Comparative Tracking Index | 250 | V | IEC 60112 |
LEXAN ML6411 polycarbonate (PC) siloxane resin, is a high flow opaque injection molding (IM) grade with very low temperature ductility characteristics. This grade offers UL94 V0 @ 1.5mm and 5VA @ 3.0mm flame retardancy based on non-chlorine, non-bromine FR systems. LEXAN ML6411 resin offers excellent processing characteristics with opportunity for shorter IM cycle times compared to standard PC. This product is available in a wide range of opaque colors and is an excellent candidate for a wide range of electrical applications.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Dielectric Strength, in oil, 3.2 mm | 26.5 | kV/mm | ASTM D149 |
Volume Resistivity | >1.E+15 | Ω.cm | IEC 60093 |
Comparative Tracking Index | 250 | V | IEC 60112 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 900 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 150 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 72 | J | ASTM D3763 |
Izod Impact, notched 80*10*3 +23°C | 60 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*3 -30°C | 15 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 90 - 100 | °C | |
Drying Time | 2 - 4 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 270 - 300 | °C | |
Nozzle Temperature | 250 - 290 | °C | |
Front - Zone 3 Temperature | 260 - 300 | °C | |
Middle - Zone 2 Temperature | 250 - 290 | °C | |
Rear - Zone 1 Temperature | 230 - 260 | °C | |
Hopper Temperature | 60 - 80 | °C | |
Mold Temperature | 60 - 90 | °C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 62 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 54 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 100 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 2500 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 95 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2600 | MPa | ASTM D790 |
Tensile Stress, yield, 50 mm/min | 62 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 58 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 5 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 100 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2350 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2350 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.19 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.8 | % | SABIC method |
Melt Flow Rate, 260°C/2.16 kgf | 7 | g/10 min | ASTM D1238 |
Density | 1.2 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 0.3 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.1 | % | ISO 62 |
Melt Volume Rate, MVR at 260°C/5.0 kg | 18 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 134 | °C | ASTM D1525 |
HDT, 1.82 MPa, 3.2mm, unannealed | 114 | °C | ASTM D648 |
HDT, 0.45 MPa, 6.4 mm, unannealed | 128 | °C | ASTM D648 |
HDT, 1.82 MPa, 6.4 mm, unannealed | 119 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 5.90E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 7.70E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 7.0E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 7.0E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
Vicat Softening Temp, Rate B/50 | 134 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 135 | °C | ISO 306 |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 125 | °C | ISO 75/Be |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 115 | °C | ISO 75/Ae |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Dielectric Strength, in oil, 3.2 mm | 26.5 | kV/mm | ASTM D149 |
Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A |
Volume Resistivity | >1.E+15 | Ω.cm | IEC 60093 |
Comparative Tracking Index | 250 | V | IEC 60112 |
Hot-Wire Ignition (HWI), PLC 2 | ≥3 | mm | UL 746A |
Hot-Wire Ignition (HWI), PLC 3 | ≥0.75 | mm | UL 746A |
High Amp Arc Ignition (HAI), PLC 0 | ≥1 | mm | UL 746A |
High Amp Arc Ignition (HAI), PLC 1 | ≥0.75 | mm | UL 746A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94-5VA Flame Class Rating | ≥3 | mm | UL 94 |
UL Recognized, 94-5VB Flame Class Rating | ≥1.7 | mm | UL 94 |
UL Recognized, 94V-0 Flame Class Rating | 1.5 | mm | UL 94 |
UL Recognized, 94V-2 Flame Class Rating | ≥0.75 | mm | UL 94 |
Glow Wire Ignitability Temperature, 3.0 mm | 800 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature, 2.0 mm | 800 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature, 1.7 mm | 800 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature, 1.5 mm | 800 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature, 1.0 mm | 800 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature, 0.75 mm | 800 | °C | IEC 60695-2-13 |
Glow Wire Flammability Index, 3.0 mm | 960 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index, 2.0 mm | 960 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index, 1.7 mm | 960 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index, 1.5 mm | 960 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index, 1.0 mm | 960 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index, 0.75 mm | 960 | °C | IEC 60695-2-12 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 900 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 150 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 72 | J | ASTM D3763 |
Izod Impact, notched 80*10*3 +23°C | 60 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*3 -30°C | 15 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 90 - 100 | °C | |
Drying Time | 2 - 4 | Hrs | |
Drying Time (Cumulative) | ≤8 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 270 - 300 | °C | |
Nozzle Temperature | 250 - 290 | °C | |
Front - Zone 3 Temperature | 260 - 300 | °C | |
Middle - Zone 2 Temperature | 250 - 290 | °C | |
Rear - Zone 1 Temperature | 230 - 260 | °C | |
Hopper Temperature | 60 - 80 | °C | |
Mold Temperature | 60 - 90 | °C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 62 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 54 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 100 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 2500 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 95 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2600 | MPa | ASTM D790 |
Tensile Stress, yield, 50 mm/min | 62 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 58 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 5 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 100 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2350 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2350 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.19 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.8 | % | SABIC method |
Melt Flow Rate, 260°C/2.16 kgf | 7 | g/10 min | ASTM D1238 |
Density | 1.2 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 0.3 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.1 | % | ISO 62 |
Melt Volume Rate, MVR at 260°C/5.0 kg | 18 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 134 | °C | ASTM D1525 |
HDT, 1.82 MPa, 3.2mm, unannealed | 114 | °C | ASTM D648 |
HDT, 0.45 MPa, 6.4 mm, unannealed | 128 | °C | ASTM D648 |
HDT, 1.82 MPa, 6.4 mm, unannealed | 119 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 5.90E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 7.70E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 7.0E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 7.0E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
Vicat Softening Temp, Rate B/50 | 134 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 135 | °C | ISO 306 |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 125 | °C | ISO 75/Be |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 115 | °C | ISO 75/Ae |
Relative Temp Index, Elec | 100 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 100 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 100 | °C | UL 746B |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Dielectric Strength, in oil, 3.2 mm | 26.5 | kV/mm | ASTM D149 |
Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A |
Volume Resistivity | >1.E+15 | Ω.cm | IEC 60093 |
Comparative Tracking Index | 250 | V | IEC 60112 |
Hot-Wire Ignition (HWI), PLC 2 | ≥3 | mm | UL 746A |
Hot-Wire Ignition (HWI), PLC 3 | ≥0.75 | mm | UL 746A |
High Amp Arc Ignition (HAI), PLC 0 | ≥1 | mm | UL 746A |
High Amp Arc Ignition (HAI), PLC 1 | ≥0.75 | mm | UL 746A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94-5VA Flame Class Rating | ≥3 | mm | UL 94 |
UL Recognized, 94-5VB Flame Class Rating | ≥1.7 | mm | UL 94 |
UL Recognized, 94V-0 Flame Class Rating | 1.5 | mm | UL 94 |
UL Recognized, 94V-2 Flame Class Rating | ≥0.75 | mm | UL 94 |
Glow Wire Ignitability Temperature, 3.0 mm | 800 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature, 2.0 mm | 800 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature, 1.7 mm | 800 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature, 1.5 mm | 800 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature, 1.0 mm | 800 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature, 0.75 mm | 800 | °C | IEC 60695-2-13 |
Glow Wire Flammability Index, 3.0 mm | 960 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index, 2.0 mm | 960 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index, 1.7 mm | 960 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index, 1.5 mm | 960 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index, 1.0 mm | 960 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index, 0.75 mm | 960 | °C | IEC 60695-2-12 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 900 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 150 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 72 | J | ASTM D3763 |
Izod Impact, notched 80*10*3 +23°C | 60 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*3 -30°C | 15 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 90 - 100 | °C | |
Drying Time | 2 - 4 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 270 - 300 | °C | |
Nozzle Temperature | 250 - 290 | °C | |
Front - Zone 3 Temperature | 260 - 300 | °C | |
Middle - Zone 2 Temperature | 250 - 290 | °C | |
Rear - Zone 1 Temperature | 230 - 260 | °C | |
Hopper Temperature | 60 - 80 | °C | |
Mold Temperature | 60 - 90 | °C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 62 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 54 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 100 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 2500 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 95 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2600 | MPa | ASTM D790 |
Tensile Stress, yield, 50 mm/min | 62 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 58 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 5 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 100 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2350 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2350 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.19 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.8 | % | SABIC method |
Melt Flow Rate, 260°C/2.16 kgf | 7 | g/10 min | ASTM D1238 |
Melt Flow Rate, 300°C/1.2 kgf | 15 | g/10 min | ASTM D1238 |
Density | 1.2 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 0.3 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.1 | % | ISO 62 |
Melt Volume Rate, MVR at 260°C/5.0 kg | 18 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 134 | °C | ASTM D1525 |
HDT, 1.82 MPa, 3.2mm, unannealed | 114 | °C | ASTM D648 |
HDT, 0.45 MPa, 6.4 mm, unannealed | 128 | °C | ASTM D648 |
HDT, 1.82 MPa, 6.4 mm, unannealed | 119 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 5.90E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 7.70E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 7.0E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 7.0E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
Vicat Softening Temp, Rate B/50 | 134 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 135 | °C | ISO 306 |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 125 | °C | ISO 75/Be |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 115 | °C | ISO 75/Ae |
Relative Temp Index, Elec | 100 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 100 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 100 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.