ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A |
Hot-Wire Ignition (HWI), PLC 3 | 1.5 | mm | UL 746A |
High Amp Arc Ignition (HAI), PLC 0 | 1.5 | mm | UL 746A |
XHT3143 is a high flow, UV stabilized, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A |
Hot-Wire Ignition (HWI), PLC 3 | 1.5 | mm | UL 746A |
High Amp Arc Ignition (HAI), PLC 0 | 1.5 | mm | UL 746A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
Glow Wire Ignitability Temperature, 3.0 mm | 875 | °C | IEC 60695-2-13 |
Glow Wire Flammability Index, 3.0 mm | 960 | °C | IEC 60695-2-12 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 97 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 55 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 68 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*3 +23°C | 9 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*3 -30°C | 9 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 11 | kJ/m² | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 9 | kJ/m² | ISO 179/1eA |
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 135 | °C | |
Drying Time | 4 - 6 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 290 - 325 | °C | |
Nozzle Temperature | 285 - 320 | °C | |
Front - Zone 3 Temperature | 290 - 325 | °C | |
Middle - Zone 2 Temperature | 280 - 310 | °C | |
Rear - Zone 1 Temperature | 270 - 300 | °C | |
Mold Temperature | 95 - 130 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 40 - 90 | rpm | |
Shot to Cylinder Size | 40 - 60 | % | |
Vent Depth | 0.025 - 0.08 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 70 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 55 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 70 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 2700 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2600 | MPa | ASTM D790 |
Tensile Stress, yield, 50 mm/min | 70 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 60 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 70 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2500 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 80 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2500 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.2 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.6 - 0.9 | % | SABIC method |
Melt Flow Rate, 330°C/2.16 kgf | 33 | g/10 min | ASTM D1238 |
Density | 1.2 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 0.3 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.3 | % | ISO 62 |
Melt Volume Rate, MVR at 330°C/2.16kg | 30 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 170 | °C | ASTM D1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed | 166 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 156 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 6.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 6.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 6.E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 6.E-05 | 1/°C | ISO 11359-2 |
Vicat Softening Temp, Rate B/50 | 168 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 170 | °C | ISO 306 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 152 | °C | ISO 75/Af |
Relative Temp Index, Elec | 150 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 130 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 150 | °C | UL 746B |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A |
Hot-Wire Ignition (HWI), PLC 3 | 1.5 | mm | UL 746A |
High Amp Arc Ignition (HAI), PLC 0 | 1.5 | mm | UL 746A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
Glow Wire Ignitability Temperature, 3.0 mm | 875 | °C | IEC 60695-2-13 |
Glow Wire Flammability Index, 3.0 mm | 960 | °C | IEC 60695-2-12 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 97 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 55 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 68 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*3 +23°C | 9 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*3 -30°C | 9 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 11 | kJ/m² | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 9 | kJ/m² | ISO 179/1eA |
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 135 | °C | |
Drying Time | 4 - 6 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 290 - 325 | °C | |
Nozzle Temperature | 285 - 320 | °C | |
Front - Zone 3 Temperature | 290 - 325 | °C | |
Middle - Zone 2 Temperature | 280 - 310 | °C | |
Rear - Zone 1 Temperature | 270 - 300 | °C | |
Mold Temperature | 95 - 130 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 40 - 90 | rpm | |
Shot to Cylinder Size | 40 - 60 | % | |
Vent Depth | 0.025 - 0.08 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 70 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 55 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 70 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 2700 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2600 | MPa | ASTM D790 |
Tensile Stress, yield, 50 mm/min | 70 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 60 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 70 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2500 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 80 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2500 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.2 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.6 - 0.9 | % | SABIC method |
Melt Flow Rate, 330°C/2.16 kgf | 33 | g/10 min | ASTM D1238 |
Density | 1.2 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 0.3 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.3 | % | ISO 62 |
Melt Volume Rate, MVR at 330°C/2.16kg | 30 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 170 | °C | ASTM D1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed | 166 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 156 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 6.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 6.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 6.E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 6.E-05 | 1/°C | ISO 11359-2 |
Vicat Softening Temp, Rate B/50 | 168 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 170 | °C | ISO 306 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 152 | °C | ISO 75/Af |
Relative Temp Index, Elec | 150 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 130 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 150 | °C | UL 746B |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A |
Hot-Wire Ignition (HWI), PLC 3 | 1.5 | mm | UL 746A |
High Amp Arc Ignition (HAI), PLC 0 | 1.5 | mm | UL 746A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
Glow Wire Ignitability Temperature, 3.0 mm | 875 | °C | IEC 60695-2-13 |
Glow Wire Flammability Index, 3.0 mm | 960 | °C | IEC 60695-2-12 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 97 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 55 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 68 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*3 +23°C | 9 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*3 -30°C | 9 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 11 | kJ/m² | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 9 | kJ/m² | ISO 179/1eA |
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 135 | °C | |
Drying Time | 4 - 6 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 290 - 325 | °C | |
Nozzle Temperature | 285 - 320 | °C | |
Front - Zone 3 Temperature | 290 - 325 | °C | |
Middle - Zone 2 Temperature | 280 - 310 | °C | |
Rear - Zone 1 Temperature | 270 - 300 | °C | |
Mold Temperature | 95 - 130 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 40 - 90 | rpm | |
Shot to Cylinder Size | 40 - 60 | % | |
Vent Depth | 0.025 - 0.08 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 70 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 55 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 70 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 2700 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 120 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2600 | MPa | ASTM D790 |
Tensile Stress, yield, 50 mm/min | 70 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 60 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 70 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2500 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 80 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2500 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.2 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.6 - 0.9 | % | SABIC method |
Melt Flow Rate, 330°C/2.16 kgf | 33 | g/10 min | ASTM D1238 |
Density | 1.2 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 0.3 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.3 | % | ISO 62 |
Melt Volume Rate, MVR at 330°C/2.16kg | 30 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 170 | °C | ASTM D1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed | 166 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 156 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 6.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 6.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 6.E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 6.E-05 | 1/°C | ISO 11359-2 |
Vicat Softening Temp, Rate B/50 | 168 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 170 | °C | ISO 306 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 152 | °C | ISO 75/Af |
Relative Temp Index, Elec | 150 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 130 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 150 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.