LEXAN DSL1120 compound is based on Polycarbonate (PC) resin containing 20% glass bead. Added features of this grade include: Flame Retardant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94V-0 Flame Class Rating | 3 | mm | UL 94 |
| UL Recognized, 94V-1 Flame Class Rating | ≥1.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Melt Temperature | 290 - 310 | °C | |
| Nozzle Temperature | 280 - 305 | °C | |
| Front - Zone 3 Temperature | 290 - 310 | °C | |
| Middle - Zone 2 Temperature | 275 - 300 | °C | |
| Rear - Zone 1 Temperature | 265 - 290 | °C | |
| Mold Temperature | 70 - 95 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Flexural Stress, yld, 2.6 mm/min, 100 mm span | 88 | MPa | ASTM D790 |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 2732 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Melt Flow Rate, 300°C/1.2 kgf | 9.6 | g/10 min | ASTM D1238 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Ash content | 19 | Wt. % | - |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 6.4 mm, unannealed | 133 | °C | ASTM D648 |
| Relative Temp Index, Elec | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |