LEXAN LF1000 compound is based on Polycarbonate (PC) resin containing 10% PTFE. Added features of this grade include: Wear Resistant, Flame Retardant and Easy Molding.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 184 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 48 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 290 - 315 | °C | |
| Nozzle Temperature | 275 - 305 | °C | |
| Front - Zone 3 Temperature | 275 - 305 | °C | |
| Middle - Zone 2 Temperature | 270 - 280 | °C | |
| Rear - Zone 1 Temperature | 270 - 280 | °C | |
| Mold Temperature | 70 - 105 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Shot to Cylinder Size | 40 - 60 | % | |
| Vent Depth | 0.025 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 50 mm/min | 61 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 90 | % | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 92 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2350 | MPa | ASTM D790 |
| Taber Abrasion, CS-17, 1 kg | 7 | mg/1000cy | ASTM D1044 |
| Coefficient of Friction on self, Static | 0.26 | - | ASTM D1894 |
| Coefficient of Friction on steel, Static | 0.24 | - | ASTM D1894 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.26 | - | ASTM D792 |
| Water Absorption, (23°C/24hrs) | 0.15 | % | ASTM D570 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 6.4 mm, unannealed | 137 | °C | ASTM D648 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+16 | Ω | ASTM D257 |
| Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 0 | ≥3.3 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 2 | ≥1.7 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 2 | ≥3.3 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 3 | ≥1.7 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 2 | PLC Code | UL 746A |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D495 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94V-0 Flame Class Rating | 1.7 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 184 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 48 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 290 - 315 | °C | |
| Nozzle Temperature | 275 - 305 | °C | |
| Front - Zone 3 Temperature | 275 - 305 | °C | |
| Middle - Zone 2 Temperature | 270 - 280 | °C | |
| Rear - Zone 1 Temperature | 270 - 280 | °C | |
| Mold Temperature | 70 - 105 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield | 66 | MPa | SABIC - Japan Method |
| Tensile Strain, break | 220 - 220 | % | SABIC - Japan Method |
| Flexural Stress | 84 | MPa | ASTM D790 |
| Flexural Modulus | 2150 | MPa | ASTM D790 |
| Hardness, Rockwell R | 118 | - | ASTM D785 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.26 | - | ASTM D792 |
| Water Absorption, (23°C/24hrs) | 0.15 | % | ASTM D570 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 136 | °C | ASTM D648 |
| CTE, -30°C to 30°C | 0.00005 - 0.00007 | 1/°C | TMA |
| Relative Temp Index, Elec | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |