FXD153 is an Extrusion / Blow molding grade in a Diffusion effect, which is part of the VisualFX family. These effects have been developed to meet increasing Aesthetic demands in the Marketplace. Color Package may affect properties, Application testing always reccomended.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2 - 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Minimum Moisture Content | 0.01 | % | |
| Melt Temperature (Parison) | 265 - 280 | °C | |
| Barrel - Zone 1 Temperature | 260 - 290 | °C | |
| Barrel - Zone 2 Temperature | 260 - 290 | °C | |
| Barrel - Zone 3 Temperature | 260 - 290 | °C | |
| Barrel - Zone 4 Temperature | 260 - 290 | °C | |
| Adapter - Zone 5 Temperature | 260 - 290 | °C | |
| Mold Temperature | 60 - 100 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 3204 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 748 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 48 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 320 - 345 | °C | |
| Nozzle Temperature | 315 - 340 | °C | |
| Front - Zone 3 Temperature | 320 - 345 | °C | |
| Middle - Zone 2 Temperature | 310 - 330 | °C | |
| Rear - Zone 1 Temperature | 300 - 320 | °C | |
| Mold Temperature | 80 - 115 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Shot to Cylinder Size | 40 - 60 | % | |
| Vent Depth | 0.025 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 50 mm/min | 62 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 66 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 7 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 110 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 2340 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 93 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2340 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.2 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
| Melt Flow Rate, 300°C/1.2 kgf | 2.5 | g/10 min | ASTM D1238 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Vicat Softening Temp, Rate B/50 | 157 | °C | ASTM D1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 138 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 132 | °C | ASTM D648 |
| CTE, -40°C to 40°C, xflow | 6.8E-05 | 1/°C | ASTM E831 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 3204 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 748 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 48 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 320 - 345 | °C | |
| Nozzle Temperature | 315 - 340 | °C | |
| Front - Zone 3 Temperature | 320 - 345 | °C | |
| Middle - Zone 2 Temperature | 310 - 330 | °C | |
| Rear - Zone 1 Temperature | 300 - 320 | °C | |
| Mold Temperature | 80 - 115 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Shot to Cylinder Size | 40 - 60 | % | |
| Vent Depth | 0.025 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 50 mm/min | 62 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 66 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 7 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 110 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 2340 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 93 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2340 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.2 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
| Melt Flow Rate, 300°C/1.2 kgf | 2.5 | g/10 min | ASTM D1238 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Vicat Softening Temp, Rate B/50 | 157 | °C | ASTM D1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 138 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 132 | °C | ASTM D648 |
| CTE, -40°C to 40°C, xflow | 6.8E-05 | 1/°C | ASTM E831 |