LEXAN FXD9332T is based on Polycarbonate (PC) copolymer resin. It is a flame-retardant and UV stabilized resin suitable for extrusion. This resin is available in a single translucent color and enables a medium fine surface texture when extruded in sheet, pipe and profiles. This flame retardant resin is EN45545 R4 compliant and is targeted for train lighting cover applications (category R4).
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2 - 4 | Hrs | |
| Barrel - Zone 1 Temperature | 260 - 300 | °C | |
| Barrel - Zone 2 Temperature | 260 - 290 | °C | |
| Barrel - Zone 3 Temperature | 260 - 290 | °C | |
| Adapter Temperature | 100 - 120 | °C | |
| Die Temperature | 240 - 280 | °C | |
| Melt Temperature | 260 - 300 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Oxygen Index (LOI) | 36 | % | ISO 4589 |
| Lateral Flame Spread, CFE | >13 | kW/m² | ISO 5658-2 |
| Smoke toxicity, CITG (8 min), 50 kW/m2 | <- 0.7 | - | ISO 5659-2 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*3 -30°C | 100 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*3 +23°C | 6 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 5 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 5 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | 100 | kJ/m² | ISO 179/1eU |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 50 mm/min | 70 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 55 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | >50 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2450 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 100 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2400 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar, flow | 0.5 - 0.8 | % | SABIC method |
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 300°C/2.16 kg | 7 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 136 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 137 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 131 | °C | ISO 75/Be |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 120 | °C | ISO 75/Af |