FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | 0.4 | mm | UL 94 |
Opaque EXL, UV-Stabilized & light shielding capability (Wall thickness >0.8mm), for portable electronics device enclosure application. Only available in white, grey and limited pastel colors. Consult CIC or PM for color availability & limitation.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | 0.4 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 766 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 640 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 68 | J | ASTM D3763 |
Izod Impact, notched 80*10*4 +23°C | 56 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C | 46 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 55 | kJ/m² | ISO 179/1eA |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 3 - 4 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 295 - 315 | °C | |
Nozzle Temperature | 290 - 310 | °C | |
Front - Zone 3 Temperature | 295 - 315 | °C | |
Middle - Zone 2 Temperature | 280 - 305 | °C | |
Rear - Zone 1 Temperature | 260 - 280 | °C | |
Hopper Temperature | 60 - 80 | °C | |
Mold Temperature | 70 - 95 | °C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 52 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 54 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 84 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 2030 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 86 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2050 | MPa | ASTM D790 |
Tensile Stress, yield, 50 mm/min | 52 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 47 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 5 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 75 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2000 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 83 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2110 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.28 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.8 | % | SABIC method |
Melt Flow Rate, 300°C/1.2 kgf | 11 | g/10 min | ASTM D1238 |
Density | 1.28 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 0.17 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 |
Melt Volume Rate, MVR at 300°C/1.2 kg | 10 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 138 | °C | ASTM D1525 |
HDT, 1.82 MPa, 3.2mm, unannealed | 121 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 7.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 6.73E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 7.02E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 8.23E-05 | 1/°C | ISO 11359-2 |
Vicat Softening Temp, Rate B/50 | 138 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 146 | °C | ISO 306 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 118 | °C | ISO 75/Af |
Relative Temp Index, Elec | 80 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | 0.4 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 766 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 640 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 68 | J | ASTM D3763 |
Izod Impact, notched 80*10*4 +23°C | 56 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C | 46 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 55 | kJ/m² | ISO 179/1eA |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 3 - 4 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 295 - 315 | °C | |
Nozzle Temperature | 290 - 310 | °C | |
Front - Zone 3 Temperature | 295 - 315 | °C | |
Middle - Zone 2 Temperature | 280 - 305 | °C | |
Rear - Zone 1 Temperature | 260 - 280 | °C | |
Hopper Temperature | 60 - 80 | °C | |
Mold Temperature | 70 - 95 | °C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 52 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 54 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 84 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 2030 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 86 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2050 | MPa | ASTM D790 |
Tensile Stress, yield, 50 mm/min | 52 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 47 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 5 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 75 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2000 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 83 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2110 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.28 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.8 | % | SABIC method |
Melt Flow Rate, 300°C/1.2 kgf | 11 | g/10 min | ASTM D1238 |
Density | 1.28 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 0.17 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 |
Melt Volume Rate, MVR at 300°C/1.2 kg | 10 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 138 | °C | ASTM D1525 |
HDT, 1.82 MPa, 3.2mm, unannealed | 121 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 7.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 6.73E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 7.02E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 8.23E-05 | 1/°C | ISO 11359-2 |
Vicat Softening Temp, Rate B/50 | 138 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 146 | °C | ISO 306 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 118 | °C | ISO 75/Af |
Relative Temp Index, Elec | 80 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | 0.4 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 766 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 640 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 68 | J | ASTM D3763 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 3 - 4 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 295 - 315 | °C | |
Nozzle Temperature | 290 - 310 | °C | |
Front - Zone 3 Temperature | 295 - 315 | °C | |
Middle - Zone 2 Temperature | 280 - 305 | °C | |
Rear - Zone 1 Temperature | 260 - 280 | °C | |
Hopper Temperature | 60 - 80 | °C | |
Mold Temperature | 70 - 95 | °C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 52 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 54 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 84 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 2030 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 86 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2050 | MPa | ASTM D790 |
Tensile Stress, yield, 50 mm/min | 52 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 47 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 5 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 75 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2000 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 83 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2110 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.28 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.8 | % | SABIC method |
Melt Flow Rate, 300°C/1.2 kgf | 11 | g/10 min | ASTM D1238 |
Density | 1.28 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 0.17 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 |
Melt Volume Rate, MVR at 300°C/1.2 kg | 10 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 138 | °C | ASTM D1525 |
HDT, 1.82 MPa, 3.2mm, unannealed | 121 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 7.E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 6.73E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 7.02E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 8.23E-05 | 1/°C | ISO 11359-2 |
Vicat Softening Temp, Rate B/50 | 138 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 146 | °C | ISO 306 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 118 | °C | ISO 75/Af |
Relative Temp Index, Elec | 80 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |