Opaque EXL, UV-Stabilized & light shielding capability, for portable electronics device enclosure application. Only available in white, grey and limited pastel colors. Consult CIC or PM for color availability & limitation.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 532 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 295 - 315 | °C | |
| Nozzle Temperature | 290 - 310 | °C | |
| Front - Zone 3 Temperature | 295 - 315 | °C | |
| Middle - Zone 2 Temperature | 280 - 305 | °C | |
| Rear - Zone 1 Temperature | 260 - 280 | °C | |
| Hopper Temperature | 60 - 80 | °C | |
| Mold Temperature | 70 - 95 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 50 mm/min | 52 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 46 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 68 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2030 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 80 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1970 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.3 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 12 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 114 | °C | ASTM D648 |