IFX121RA is a low viscosity, infra-red absorbing, polycarbonate grade-color
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 3204 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 694 | J/m | ASTM D256 |
| Tensile Impact Strength, Type S | 546 | kJ/m² | ASTM D1822 |
| Falling Dart Impact (D 3029), 23°C | 169 | J | ASTM D3029 |
| Instrumented Dart Impact Energy @ peak, 23°C | 62 | J | ASTM D3763 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 48 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 280 - 305 | °C | |
| Nozzle Temperature | 275 - 300 | °C | |
| Front - Zone 3 Temperature | 280 - 305 | °C | |
| Middle - Zone 2 Temperature | 270 - 295 | °C | |
| Rear - Zone 1 Temperature | 260 - 280 | °C | |
| Mold Temperature | 70 - 95 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Shot to Cylinder Size | 40 - 60 | % | |
| Vent Depth | 0.025 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 50 mm/min | 62 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 68 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 7 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 125 | % | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 96 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2340 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.2 | - | ASTM D792 |
| Specific Volume | 0.83 | cm³/g | ASTM D792 |
| Water Absorption, (23°C/24hrs) | 0.15 | % | ASTM D570 |
| Water Absorption, (23°C/Saturated) | 0.35 | % | ASTM D570 |
| Water Absorption, equilibrium, 100°C | 0.58 | % | ASTM D570 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
| Melt Flow Rate, 300°C/1.2 kgf | 18.5 | g/10 min | ASTM D1238 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Vicat Softening Temp, Rate B/50 | 154 | °C | ASTM D1525 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 137 | °C | ASTM D648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 129 | °C | ASTM D648 |
| CTE, -40°C to 95°C, flow | 6.84E-05 | 1/°C | ASTM E831 |
| Specific Heat | 1.25 | J/g-°C | ASTM C351 |
| Thermal Conductivity | 0.25 | W/m-°C | ASTM C177 |