COLORCOMP 9X02694J compound is based on Polyphenylsulfone (PPSU). Added features of this grade include High Heat Resistance, Healthcare, Low Extractable.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 690 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 2.5 | Hrs | |
| Maximum Moisture Content | 0.05 | % | |
| Melt Temperature | 360 - 390 | °C | |
| Mold Temperature | 140 - 160 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Modulus, 50 mm/min | 2340 | MPa | ASTM D638 |
| Tensile Stress, yld, Type I, 50 mm/min | 69.6 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 7.2 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 90 | % | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2410 | MPa | ASTM D790 |
| Flexural Stress at 5% strain, 1.3 mm/min, 50 mm span | 91 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.29 | - | ASTM D792 |
| Water Absorption, (23°C/24hrs) | 0.37 | % | ASTM D570 |
| Water Absorption, (23°C/Saturated) | 1.1 | % | ASTM D570 |
| Melt Flow Rate, 365°C/5.0 kgf | 14.5 | g/10 min | ASTM D1238 |
| Mold Shrinkage, flow | 0.7 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 207 | °C | ASTM D648 |
| CTE, -30°C to 30°C, flow | 5.5E-05 | 1/°C | ASTM D696 |