LNP™ COLORCOMP™ Compound 9X20038

LNP COLORCOMP 9X20038 compound is based on Polycarbonate / Acrylonitrile styrene acrylate (PC/ASA) blend. Added features of this grade include; increased flow, improved release and easy processing.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate + ASA (PC+ASA)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Aesthetics/Visual effects
Enhanced mold release
Good Processability
High Flow
Impact resistant
No PFAS intentionally added

Industry

Material previously used in

Electrical

Applications

Possible usage of material

EV/HEV Charging System

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Glow Wire Flammability Index, 3.0 mm	775	°C	IEC 60695-2-12
Glow Wire Flammability Index, 2.5 mm	750	°C	IEC 60695-2-12
Glow Wire Flammability Index, 2.0 mm	750	°C	IEC 60695-2-12
Glow Wire Ignitability Temperature, 3.0 mm	800	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 2.5 mm	775	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 2.0 mm	775	°C	IEC 60695-2-13

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	580	J/m	ASTM D256
Izod Impact, notched, -30°C	140	J/m	ASTM D256
Izod Impact, unnotched, 23°C	NB	J/m	ASTM D4812
Izod Impact, unnotched, -30°C	NB	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	50	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	18	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	NB	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -30°C*	NB	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	60	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	15	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	NB	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80104 sp=62mm*	NB	kJ/m²	ISO 179/1eU
Multi-Axial Instrumented Impact Total Energy, 23°C	110	J	ISO 6603-2
Multi-Axial Instrumented Impact Energy @ peak, 23°C	90	J	ISO 6603-2
Multi-Axial Instrumented Impact Total Energy, -30°C	100	J	ISO 6603-2
Multi-Axial Instrumented Impact Energy @ peak, -30°C	95	J	ISO 6603-2

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100 - 120	°C
Drying Time	2 - 4	Hrs
Drying Time (Cumulative)	12	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	260 - 290	°C
Nozzle Temperature	240 - 280	°C
Front - Zone 3 Temperature	250 - 290	°C
Middle - Zone 2 Temperature	250 - 290	°C
Rear - Zone 1 Temperature	230 - 260	°C
Hopper Temperature	40 - 80	°C
Mold Temperature	60 - 90	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	55	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	5	%	ASTM D638
Tensile Nominal Strain, brk, Type I, 50 mm/min	>75	%	ASTM D638
Tensile Modulus, 50 mm/min	2200	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	84	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2200	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	55	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5	%	ISO 527
Tensile Strain, break, 50 mm/min	>75	%	ISO 527
Tensile Modulus, 1 mm/min	2100	MPa	ISO 527
Flexural Strength, 2 mm/min	76	MPa	ISO 178
Flexural Modulus, 2 mm/min	2500	MPa	ISO 178
Ball Indentation Hardness, H358/30	120	MPa	ISO 2039-1
Hardness, Rockwell R	115	-	ISO 2039-2

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.17	-	ASTM D792
Melt Flow Rate, 260°C/5.0 kgf	35	g/10 min	ASTM D1238
Density	1.17	g/cm³	ISO 1183
Melt Volume Rate, MVR at 260°C/5.0 kg	33	cm³/10 min	ISO 1133
Water Absorption, (23°C/saturated)	0.1	%	ISO 62-1
Mold Shrinkage, flow	0.5 - 0.7	%	SABIC method
Mold Shrinkage, xflow	0.5 - 0.7	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	111	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	128	°C	ASTM D648
Vicat Softening Temp, Rate B/50	129	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	130	°C	ASTM D1525
CTE, 23°C to 60°C, flow	8.5e-5	1/°C	ASTM E831
CTE, 23°C to 60°C, xflow	8.5e-5	1/°C	ASTM E831
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	112	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	130	°C	ISO 75/Bf
Vicat Softening Temp, Rate B/50	129	°C	ISO 306
Vicat Softening Temp, Rate B/120	130	°C	ISO 306
CTE, 23°C to 60°C, flow	8.5e-5	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	8.5e-5	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	pass	-	IEC 60695-10-2

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES