LNP COLORCOMP 9X99415 compound is based on Polyether Block Amide resin.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 120 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 20 | kJ/m² | ISO 179/1eA |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Melt Temperature | 260 | °C | |
| Mold Temperature | 164 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 50 mm/min | 22 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 20 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | ≥50 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 390 | MPa | ISO 527 |
| Hardness, Shore D | 61 | - | ISO 868 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 1.1 | % | ISO 62 |
| Water Absorption, (23°C/24hrs) | 0.7 | % | ISO 62-1 |
| Mold Shrinkage, flow, 24 hrs | 1.2 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1.5 | % | ISO 294 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Melting Temperature | 172 | °C | ISO 11357-3 |
| Vicat Softening Temp, Rate B/50 | 164 | °C | ISO 306 |