LNP™ COLORCOMP™ Compound AX03575

LNP COLORCOMP AX03575 is a compound based on Acrylonitrile Butadiene Styrene (ABS). Added features of this grade include low gloss and high flow.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Acrylonitrile Butadiene Styrene (ABS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Good Processability
No PFAS intentionally added

Industry

Material previously used in

Automotive Interiors
Industrial General

Applications

Possible usage of material

Console
Document Handling
Enclosures

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	170	J/m	ASTM D256

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80 - 95	°C
Drying Time	2 - 4	Hrs
Drying Time (Cumulative)	8	Hrs
Maximum Moisture Content	0.1	%
Melt Temperature	220 - 260	°C
Nozzle Temperature	220 - 260	°C
Front - Zone 3 Temperature	215 - 240	°C
Middle - Zone 2 Temperature	205 - 225	°C
Rear - Zone 1 Temperature	190 - 210	°C
Mold Temperature	50 - 70	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	30 - 60	rpm
Shot to Cylinder Size	50 - 70	%
Vent Depth	0.035 - 0.051	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 50 mm/min	2210	MPa	ASTM D638
Tensile Stress, yld, Type I, 50 mm/min	36.5	MPa	ASTM D638
Flexural Stress	72	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2410	MPa	ASTM D790
Hardness, Rockwell R	105	-	ASTM D785
Tensile Stress, yield, 50 mm/min	39	MPa	ISO 527
Flexural Modulus, 2 mm/min	2430	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.05	-	ASTM D792
Melt Flow Rate, 230°C/3.8 kg	7	g/10 min	ASTM D1238
Melt Flow Rate, 220°C/10.0 kgf	21	g/10 min	ASTM D1238

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	90	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm	100	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	76	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, annealed	95	°C	ASTM D648
CTE, -40°C to 40°C, flow	9.0E-5	1/°C	ASTM E831
Vicat Softening Temp, Rate A/120	107	°C	ASTM D1525
Vicat Softening Temp, Rate B/50	96	°C	ISO 306

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES