LNP™ COLORCOMP™ Compound AX98561

LNP COLORCOMP AX98561 is a compound based on Acrylonitrile Butadiene Styrene (ABS). Added features of this grade include low gloss and a good balance of physical properties.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Acrylonitrile Butadiene Styrene (ABS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Aesthetics/Visual effects
Good Processability
No PFAS intentionally added

Industry

Material previously used in

Automotive Interiors
Commercial Appliance
Electrical
Home Appliances
Home Decoration
Industrial General
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Console
Document Handling
Enclosures

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	220	J/m	ASTM D256
Izod Impact, notched, -40°C	48	J/m	ASTM D256

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80 - 95	°C
Drying Time	2 - 4	Hrs
Drying Time (Cumulative)	8	Hrs
Maximum Moisture Content	0.1	%
Melt Temperature	220 - 260	°C
Nozzle Temperature	220 - 260	°C
Front - Zone 3 Temperature	215 - 240	°C
Middle - Zone 2 Temperature	205 - 225	°C
Rear - Zone 1 Temperature	190 - 210	°C
Mold Temperature	50 - 70	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	30 - 60	rpm
Shot to Cylinder Size	50 - 70	%
Vent Depth	0.038 - 0.051	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	47	MPa	ASTM D638
Tensile Modulus, 5 mm/min	2620	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	74	MPa	ASTM D790
Hardness, Rockwell R	112	-	ASTM D785

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.06	-	ASTM D792
Melt Flow Rate, 230°C/3.8 kg	5	g/10 min	ASTM D1238
Melt Flow Rate, 220°C/10.0 kgf	13	g/10 min	ASTM D1238
Mold Shrinkage, flow, 3.2 mm	0.4 - 0.6	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	93	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	86	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, annealed	95.6	°C	ASTM D648
CTE, -40°C to 40°C, flow	8.1E-5	1/°C	ASTM E831
Vicat Softening Temp, Rate A/120	107	°C	ASTM D1525

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES