LNP COLORCOMP AX98567H compound is based on Acrylonitrile Butadiene Styrene (ABS) resin. Added features of this grade include: Healthcare.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Volume Resistivity | 1.E+16 | Ω.cm | IEC 60093 |
| Surface Resistivity, ROA | 1.E+16 | Ω | IEC 60093 |
| Hot-Wire Ignition (HWI), PLC 4 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥1.5 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A |
| Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D495 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Charpy Impact, unnotched, -30°C | 70 | kJ/m² | ISO 179/2C |
| Izod Impact, notched 80*10*4 +23°C | 12 | kJ/m² | ISO 180/1A |
| Charpy Impact, notched, 23°C | 11 | kJ/m² | ISO 179/2C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.05 - 0.1 | % | |
| Melt Temperature | 260 | °C | |
| Front - Zone 3 Temperature | 265 - 275 | °C | |
| Middle - Zone 2 Temperature | 230 - 245 | °C | |
| Rear - Zone 1 Temperature | 205 - 215 | °C | |
| Mold Temperature | 70 - 80 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 5 mm/min | 52 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 15 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2500 | MPa | ISO 527 |
| Flexural Stress | 75 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2600 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.06 | - | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.4 - 0.6 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.4 - 0.6 | % | ISO 294 |
| Melt Volume Rate, MVR at 220°C/10.0 kg | 16 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 230°C/10.0 kg | 27 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, 23°C to 60°C, flow | 8.E-05 | 1/°C | ISO 11359-2 |
| Relative Temp Index, Elec | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 80 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B |