LNP™ COLORCOMP™ Compound CQ518811

LNPTM COLORCOMPTM COMPOUND CQ518811-NC is a GPPS based masterbatch for XPS foaming applications containing a nanostructured, non-mineral based additive. Typical usage levels in final foam formulations are below 5%.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polystyrene (PS)

Processing Technology

Foam Extrusion

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Good Processability
Low Specific Gravity

Industry

Material previously used in

Industrial General

Applications

Possible usage of material

Foam Extrusion

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

EXTRUSION

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	2 - 4	Hrs
Melt Temperature	180 - 240	°C
Die Temperature	80 - 140	°C

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Melt Volume Rate, MVR at 230°C/5.0 kg	22	cm³/10 min	ISO 1133
Density	1.056	g/cm³	ISO 1183

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Glass Transition Temperature (Tg)	102	°C	ISO 11357-2
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	92	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	79	°C	ISO 75/Af
Vicat Softening Temp, Rate B/50	97	°C	ISO 306
Vicat Softening Temp, Rate B/120	98	°C	ISO 306
HDT, 1.82 MPa, 3.2mm, unannealed	92	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	80	°C	ASTM D648
Vicat Softening Temp, Rate B/50	97	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	98	°C	ASTM D1525

Register for High value Multi-Point Data