LNP™ COLORCOMP™ Compound DX04401H

LNP COLORCOMP DX04401H compound is based on Polycarbonate (PC) resin. Added features of this grade include: Healthcare.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Aesthetics/Visual effects
Healthcare/Formula lock

Industry

Material previously used in

General Healthcare
Industrial Packaging
Patient Testing
Pharmaceutical Packaging and Drug Delivery
Surgical devices

Applications

Possible usage of material

Surgical Devices

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	2.E+17	Ω.cm	ASTM D257
Dielectric Constant, 1 MHz	3	-	ASTM D150
Dissipation Factor, 100 Hz	0.001	-	ASTM D150
Dissipation Factor, 1 MHz	0.002	-	ASTM D150

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	NB	J/m	ASTM D4812
Izod Impact, notched, 23°C	750	J/m	ASTM D256
*Izod Impact, notched 80104 +23°C*	75	kJ/m²	ISO 180/1A
Charpy Impact, notched, 23°C	25	kJ/m²	ISO 179/2C
Charpy Impact, notched, -30°C	12	kJ/m²	ISO 179/2C

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	305 - 325	°C
Front - Zone 3 Temperature	320 - 330	°C
Middle - Zone 2 Temperature	310 - 320	°C
Rear - Zone 1 Temperature	295 - 305	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield, 50 mm/min	62	MPa	ASTM D638
Tensile Stress, break, 50 mm/min	68	MPa	ASTM D638
Tensile Strain, yield, 50 mm/min	6	%	ASTM D638
Tensile Modulus, 50 mm/min	2210	MPa	ASTM D638
Hardness, Rockwell R	118	-	ASTM D785
Tensile Stress, yield	62	MPa	ISO 527
Tensile Stress, break	68	MPa	ISO 527
Tensile Strain, yield	6	%	ISO 527
Tensile Strain, break	150	%	ISO 527
Flexural Stress	98	MPa	ISO 178
Flexural Modulus, 2 mm/min	2400	MPa	ISO 178

OPTICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Refractive Index	1.586	-	ASTM D542
Refractive Index	1.586	-	ISO 489

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.2	-	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.15	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.5 - 0.5	%	ASTM D955
Moisture Absorption (23°C / 50% RH)	0.32	%	ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg	12	cm³/10 min	ISO 1133

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	122	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	120	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES