LNP™ COLORCOMP™ Compound DX09304C

LNP COLORCOMP DX09304C is an unfilled polycarbonate (PC) resin. Added features of this grade include: easy molding, very low level of leachable ions and low outgassing.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Good Processability
Low ionics/Outgassing/Liquid particle count
No PFAS intentionally added

Industry

Material previously used in

Electrical
Electronic Components
Material Handling
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Medical Device
Pharmaceutical Packaging & Drug Delivery
Semiconductor
data storage
hdd component
hard disk drive
hdd spoiler
hdd air diverter
hdd ramp
disk separator
dsp
foup
casette

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	790	J/m	ASTM D256
Izod Impact, unnotched, 23°C	2117	J/m	ASTM D4812
Izod Impact, notched, -30°C	108	J/m	ASTM D256
*Izod Impact, unnotched 80104 +23°C*	139	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	46.5	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	11.1	kJ/m²	ISO 180/1A
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	100.8	kJ/m²	ISO 179/1eU
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	63.3	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	11.7	kJ/m²	ISO 179/1eA

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100	°C
Drying Time	3 - 5	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	260 - 300	°C
Nozzle Temperature	260 - 300	°C
Front - Zone 3 Temperature	260 - 300	°C
Middle - Zone 2 Temperature	260 - 300	°C
Rear - Zone 1 Temperature	240 - 260	°C
Mold Temperature	80 - 120	°C
Back Pressure	0.1 - 0.5	MPa
Screw Speed	30 - 100	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Flexural Stress, yld, 1.3 mm/min, 50 mm span	94	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2210	MPa	ASTM D790
Flexural Strength, 2 mm/min	92.4	MPa	ISO 178
Flexural Modulus, 2 mm/min	2200	MPa	ISO 178
Tensile Stress, yld, Type I, 50 mm/min	60.4	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	59.1	MPa	ASTM D638
Tensile Modulus, 50 mm/min	2283	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	0.22	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	78.6	%	ASTM D638
Tensile Stress, yield, 50 mm/min	59.4	MPa	ISO 527
Tensile Stress, break, 50 mm/min	60.5	MPa	ISO 527
Tensile Modulus, 1 mm/min	2300	MPa	ISO 527
Tensile Strain, break, 50 mm/min	106	%	ISO 527

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.195	-	ASTM D792
Water Absorption, (23°C/saturated)	0.05	%	ISO 62-1
Melt Flow Rate, 300°C/1.2 kgf	22	g/10 min	ASTM D1238
Mold Shrinkage, flow	0.66	%	SABIC method
Mold Shrinkage, xflow	0.69	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	142	°C	ASTM D648
Vicat Softening Temp, Rate A/120	149	°C	ISO 306
CTE, 23°C to 80°C, flow	8.0E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	8.0E-05	1/°C	ISO 11359-2

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES