LNP™ COLORCOMP™ Compound DX09911

LNP COLORCOMP DX09911 compound is based on Polycarbonate (PC) resin. Added features of this grade include: good impact combined with good flow, good aesthetics and colorable.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Good Processability
Impact resistant
No PFAS intentionally added

Industry

Material previously used in

Automotive Interiors
Consumer Goods
Industrial General

Applications

Possible usage of material

Automotive

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	544	J/m	ASTM D256
*Izod Impact, notched 80104 +23°C*	13	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	310 - 330	°C
Front - Zone 3 Temperature	310 - 330	°C
Middle - Zone 2 Temperature	300 - 320	°C
Rear - Zone 1 Temperature	290 - 310	°C
Mold Temperature	80 - 115	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield	62	MPa	ASTM D638
Tensile Stress, break	56	MPa	ASTM D638
Tensile Strain, yield	5.3	%	ASTM D638
Tensile Strain, break	78.7	%	ASTM D638
Tensile Modulus, 50 mm/min	2060	MPa	ASTM D638
Flexural Modulus	2750	MPa	ASTM D790
Tensile Stress, yield	64	MPa	ISO 527
Tensile Stress, break	59	MPa	ISO 527
Tensile Strain, yield	5.6	%	ISO 527
Tensile Strain, break	87	%	ISO 527
Tensile Modulus, 1 mm/min	2210	MPa	ISO 527
Flexural Stress	81	MPa	ISO 178
Flexural Modulus	2300	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.2	g/cm³	ASTM D792
Mold Shrinkage, flow, 24 hrs	0.6 - 0.8	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.7 - 0.9	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	0.65	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.75	%	ISO 294
Density	1.19	g/cm³	ISO 1183
Melt Flow Rate, 300°C/6.1 kgf	15	g/10 min	ASTM D1238

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	123	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	124	°C	ISO 75/Af

Register for High value Multi-Point Data