LNP™ COLORCOMP™ Compound E1000
LNP COLORCOMP E1000 compound is based on unfilled Polyetherimide (PEI) resin.
Product Family
- LNP™ COMPOUNDS AND PC COPOLYMER RESINS
Polymer Family
- Polyetherimide (PEI)
Processing Technology
- Injection Molding
Colors
All colors are customizable. Refer our ColorXpress tool to check color availability
Features
Key characteristics of the material- Aesthetics/Visual effects
- High temperature resistance
- No PFAS intentionally added
Industry
Material previously used in- Automotive Interiors
- Commercial Appliance
- Electrical
- Home Appliances
- Mobile Phone - Computer - Tablets
- Personal Accessory
- Sport/Leisure
Applications
Possible usage of material- Building Element
Technical Datasheet Data
View different characteristics of the material at a standard test conditionsIMPACT
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
INJECTION MOLDING
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 360 - 400 | °C | |
| Rear - Zone 1 Temperature | 360 - 380 | °C | |
| Middle - Zone 2 Temperature | 370 - 390 | °C | |
| Front - Zone 3 Temperature | 380 - 400 | °C | |
| Nozzle Temperature | 390 - 400 | °C | |
| Mold Temperature | 140 - 180 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw speed (Circumferential speed) | 0.2 - 0.3 | m/s | |
| Vent Depth | 0.025 - 0.076 | mm |
MECHANICAL
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 50 mm/min | 105 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 85 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 60 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3200 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 160 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3300 | MPa | ISO 178 |
PHYSICAL
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage, flow | 0.6 | % | SABIC method |
| Density | 1.27 | g/cm³ | ISO 1183 |
THERMAL
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 190 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 105 | °C | UL 746B |
Related Documents
you can download all the related literature to this material here. If any other document is required, please contact usTechnical Data Sheets
Your PDF is downloading. Please wait.
Register for High value Multi-Point Data