LNP COLORCOMP EX14001 compound is based on unfilled Polyetherimide (PEI) resin. Added features of this grade include: Easy Molding.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 360 - 400 | °C | |
| Rear - Zone 1 Temperature | 360 - 380 | °C | |
| Middle - Zone 2 Temperature | 370 - 390 | °C | |
| Front - Zone 3 Temperature | 380 - 400 | °C | |
| Nozzle Temperature | 390 - 400 | °C | |
| Mold Temperature | 140 - 180 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw speed (Circumferential speed) | 0.2 - 0.3 | m/s | |
| Vent Depth | 0.025 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 50 mm/min | 105 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 85 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 60 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3200 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 160 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3300 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage, flow | 0.6 | % | SABIC method |
| Density | 1.27 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 190 | °C | ISO 75/Af |