LNP™ COLORCOMP™ Compound G1000LX1

LNP COLORCOMP G1000LX1 compound is based on unfilled Polysulfone (PSU) resin. Added features of this grade include: Low Extractables.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polysulfone (PSU)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Aesthetics/Visual effects
Food contact
High temperature resistance
No PFAS intentionally added

Industry

Material previously used in

Food & Beverage
Home Appliances
Industrial Packaging
Water Management

Applications

Possible usage of material

Food Processor
Medical Device
Surgical Devices
Trim

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, unnotched 80104 +23°C*	137	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	9	kJ/m²	ISO 180/1A
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	100	kJ/m²	ISO 179/1eU
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	5	kJ/m²	ISO 179/1eA
Izod Impact, unnotched, 23°C	1700	J/m	ASTM D4812
Izod Impact, notched, 23°C	50	J/m	ASTM D256

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120 - 150	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.05	%
Melt Temperature	360 - 370	°C
Front - Zone 3 Temperature	350 - 360	°C
Middle - Zone 2 Temperature	340 - 350	°C
Rear - Zone 1 Temperature	325 - 340	°C
Mold Temperature	150	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield, 50 mm/min	75	MPa	ISO 527
Tensile Stress, break, 50 mm/min	60	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	6	%	ISO 527
Tensile Strain, break, 50 mm/min	65	%	ISO 527
Tensile Modulus, 1 mm/min	2550	MPa	ISO 527
Flexural Strength, 2 mm/min	115	MPa	ISO 178
Flexural Modulus, 2 mm/min	2500	MPa	ISO 178
Tensile Stress, yld, Type I, 50 mm/min	70	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	65	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	5	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	100	%	ASTM D638
Tensile Modulus, 5 mm/min	2600	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	115	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2560	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.24	g/cm³	ISO 1183
Mold Shrinkage, flow	0.7	%	SABIC method
Mold Shrinkage, xflow	0.7	%	SABIC method
Moisture Absorption, (23°C/50% RH/24hrs)	0.1	%	ISO 62-4
Moisture Absorption, (23°C/50% RH/Equilibrium)	0.3	%	ISO 62-4
Melt Volume Rate, MVR at 345°C/2.16 kg	7.8	cm³/10 min	ISO 1133

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	180	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	170	°C	ISO 75/Af
Vicat Softening Temp, Rate B/50	185	°C	ISO 306
Vicat Softening Temp, Rate B/120	185	°C	ISO 306
CTE, 23°C to 60°C, flow	6.3E-05	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	6.5E-05	1/°C	ISO 11359-2
HDT, 0.45 MPa, 3.2 mm, unannealed	180	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	170	°C	ASTM D648

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience