LNP COLORCOMP I1000 compound is based on unfilled Nylon 6/12 resin.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Volume Resistivity | 1.E+15 | Ω.cm | ASTM D257 |
| Surface Resistivity | 1.E+12 | Ω | ASTM D257 |
| Relative Permittivity, 100 Hz | 3.6 | - | ASTM D150 |
| Relative Permittivity, 1 MHz | 3.2 | - | ASTM D150 |
| Dissipation Factor, 100 Hz | 0.02 | - | ASTM D150 |
| Dissipation Factor, 1 kHz | 0.02 | - | ASTM D150 |
| Dissipation Factor, 100 kHz | 0.014 | - | ASTM D150 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Oxygen Index (LOI) | 27 | % | ISO 4589 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.12 - 0.2 | % | |
| Melt Temperature | 270 - 275 | °C | |
| Front - Zone 3 Temperature | 270 - 280 | °C | |
| Middle - Zone 2 Temperature | 260 - 270 | °C | |
| Rear - Zone 1 Temperature | 255 - 265 | °C | |
| Mold Temperature | 65 - 95 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Strain, brk, Type I, 5 mm/min | 100 | % | ASTM D638 |
| Tensile Stress, yield, 5 mm/min | 62 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 4.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2390 | MPa | ISO 527 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.06 | - | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 1 - 3 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 1 - 3 | % | ASTM D955 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 55 | °C | ASTM D648 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 135 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 62 | °C | ISO 75/Af |