LNP™ COLORCOMP™ Compound J1000
LNP COLORCOMP J1000 compound is based on unfilled Polyethersulfone (PES) resin.
Product Family
- LNP™ COMPOUNDS AND PC COPOLYMER RESINS
Polymer Family
- Polyethersulfone (PESU)
Processing Technology
- Injection Molding
Colors
All colors are customizable. Refer our ColorXpress tool to check color availability
Features
Key characteristics of the material- Aesthetics/Visual effects
- High temperature resistance
- No PFAS intentionally added
Industry
Material previously used in- Automotive Interiors
- Commercial Appliance
- Electrical
- Home Appliances
- Mobile Phone - Computer - Tablets
- Personal Accessory
- Sport/Leisure
Applications
Possible usage of material- Electronic Components
- Oil/Gas
Technical Datasheet Data
View different characteristics of the material at a standard test conditionsIMPACT
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
INJECTION MOLDING
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.05 | % | |
| Melt Temperature | 355 - 370 | °C | |
| Front - Zone 3 Temperature | 370 - 380 | °C | |
| Middle - Zone 2 Temperature | 360 - 370 | °C | |
| Rear - Zone 1 Temperature | 345 - 355 | °C | |
| Mold Temperature | 140 - 150 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 60 - 100 | rpm |
MECHANICAL
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 50 mm/min | 91 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 67 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6.8 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2700 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 128 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2600 | MPa | ISO 178 |
PHYSICAL
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage, flow | 1 | % | SABIC method |
| Density | 1.37 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/24hrs) | 0.6 | % | ISO 62-1 |
THERMAL
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, 23°C to 60°C, flow | 5.9E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 5.9E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 216 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 201 | °C | ISO 75/Af |
Related Documents
you can download all the related literature to this material here. If any other document is required, please contact usTechnical Data Sheets
Your PDF is downloading. Please wait.
Register for High value Multi-Point Data
- Access validated product data to streamline material selection
- Get inspired by innovative application ideas
- Register for high value multi-point data and a personalized experience