IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
LNP COLORCOMP J1000ER compound is based on unfilled Polyethersulfone (PES) resin. Added features of this grade include: Easy Molding, Mold Release
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 - 150 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.05 | % | |
Melt Temperature | 355 - 370 | °C | |
Front - Zone 3 Temperature | 370 - 380 | °C | |
Middle - Zone 2 Temperature | 360 - 370 | °C | |
Rear - Zone 1 Temperature | 345 - 355 | °C | |
Mold Temperature | 140 - 150 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 60 - 100 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield, 50 mm/min | 88 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 77 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 6.6 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2700 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 129 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2600 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Mold Shrinkage, flow | 0.9 | % | SABIC method |
Density | 1.38 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/24hrs) | 1.7 | % | ISO 62-1 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 200 | °C | ISO 75/Af |