IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 53 | J/m | ASTM D256 |
LNP COLORCOMP JX09403J compound is based on Polyethersulfone (PES) resin. Added features of this grade include: Colorability, Healthcare, Low Extractables, Food Contact compliant
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 53 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Time | 4 | Hrs | |
Drying Temperature | 120 - 150 | °C | |
Maximum Moisture Content | 0.5 | % | |
Melt Temperature | 355 - 370 | °C | |
Rear - Zone 1 Temperature | 345 - 355 | °C | |
Middle - Zone 2 Temperature | 360 - 370 | °C | |
Nozzle Temperature | 370 - 380 | °C | |
Mold Temperature | 140 - 150 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 60 - 100 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Modulus, 50 mm/min | 2690 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min | 88.9 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 5 mm/min | 6.5 | % | ASTM D638 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2620 | MPa | ASTM D790 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 125 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.37 | g/cm³ | ISO 1183 |
Specific Gravity | 1.37 | - | ASTM D792 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 200 | °C | ASTM D648 |