LNP COLORCOMP M1000S compound is based on Polypropylene (PP) resin. Added features of this grade include: Heat Stabilised.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 3 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 215 - 220 | °C | |
| Front - Zone 3 Temperature | 205 - 215 | °C | |
| Middle - Zone 2 Temperature | 200 - 210 | °C | |
| Rear - Zone 1 Temperature | 195 - 205 | °C | |
| Mold Temperature | 30 - 50 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield | 28 | MPa | ISO 527 |
| Tensile Stress, break | 26 | MPa | ISO 527 |
| Tensile Strain, yield | 7 | % | ISO 527 |
| Tensile Strain, break | 40 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2160 | MPa | ISO 527 |
| Flexural Stress | 30 | MPa | ISO 178 |
| Flexural Modulus | 1600 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Melt Flow Rate, 230°C/2.16 kgf | 6 | g/10 min | ASTM D1238 |
| Density | 1.13 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 1.5 - 1.7 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 1.5 - 1.7 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 1.51 - 1.67 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1.51 - 1.67 | % | ISO 294 |
| Density | 1.12 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 130 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 94 | °C | ISO 75/Af |