LNP COLORCOMP PX99848 compound is based on Nylon 6 resin. Added features of this grade include: Heat Stabilized.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 640 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 58 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 265 - 275 | °C | |
| Front - Zone 3 Temperature | 275 - 290 | °C | |
| Middle - Zone 2 Temperature | 265 - 275 | °C | |
| Rear - Zone 1 Temperature | 250 - 260 | °C | |
| Mold Temperature | 80 - 95 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield | 76 | MPa | ASTM D638 |
| Tensile Stress, break | 76 | MPa | ASTM D638 |
| Tensile Strain, yield | 3.5 | % | ASTM D638 |
| Tensile Strain, break | 4.5 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 3460 | MPa | ASTM D638 |
| Flexural Stress | 103 | MPa | ASTM D790 |
| Flexural Modulus | 2880 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 1.3 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 1.2 - 1.4 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 1.2 - 1.4 | % | ASTM D955 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 180 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 57 | °C | ASTM D648 |