LNP COLORCOMP R1000 compound is based on unfilled Nylon 6/6 resin.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| Charpy Impact, notched, 23°C | 6 | kJ/m² | ISO 179/2C |
| Charpy Impact, notched, -30°C | 6 | kJ/m² | ISO 179/2C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 275 - 290 | °C | |
| Front - Zone 3 Temperature | 295 - 305 | °C | |
| Middle - Zone 2 Temperature | 280 - 295 | °C | |
| Rear - Zone 1 Temperature | 265 - 275 | °C | |
| Mold Temperature | 80 - 95 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield, 5 mm/min | 79 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 11 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 45 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2990 | MPa | ISO 527 |
| Flexural Stress | 33 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2900 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage, flow | 1.2 | % | SABIC method |
| Mold Shrinkage, xflow | 1.4 | % | SABIC method |
| Density | 1.14 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 200 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 70 | °C | ISO 75/Af |