IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
LNP COLORCOMP R1000S compound is based on Nylon 6/6 resin. Added features of this grade include: Heat Stabilised.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.15 - 0.25 | % | |
Melt Temperature | 265 - 275 | °C | |
Front - Zone 3 Temperature | 260 - 270 | °C | |
Middle - Zone 2 Temperature | 255 - 265 | °C | |
Rear - Zone 1 Temperature | 250 - 260 | °C | |
Mold Temperature | 60 - 100 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield | 75 | MPa | ISO 527 |
Tensile Strain, yield | 10 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 3400 | MPa | ISO 527 |
Flexural Stress | 11 | MPa | ISO 178 |
Flexural Modulus | 3200 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.22 | g/cm³ | ASTM D792 |
Density | 1.23 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 75 | °C | ISO 75/Af |