LNP™ COLORCOMP™ Compound W1000Z

LNP COLORCOMP W1000Z compound is based on Polybutylene Terephthalate (PBT) resin. Added features of this grade include: Healthcare, High Viscosity suitable for Extrusion.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polybutylene Terephthalate (PBT)

Processing Technology

Compounding Extrusion
Extrusion

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Aesthetics/Visual effects
No PFAS intentionally added

Industry

Material previously used in

Automotive Interiors
Commercial Appliance
Home Appliances
Home Decoration
Mobile Phone - Computer - Tablets
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Air Filtration
Commercial Storage/Cookware
Electronic Components
Food Processor
Heavy Vehicles
Lab Ware and Clinical Diagnostics
Medical Device
Personal Care
Pharmaceutical Packaging & Drug Delivery
Servingware
Vending Machine
Water Treatment/Filtration
Wiring Devices
Wire & cable

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

COMPOUNDING EXTRUSION

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110 - 120	°C
Drying Time	4 - 6	Hrs
Drying Time (Cumulative)	8	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	245 - 260	°C
Barrel - Zone 1 Temperature	200 - 230	°C
Barrel - Zone 2 Temperature	240 - 255	°C
Barrel - Zone 3 Temperature	240 - 275	°C
Barrel - Zone 4 Temperature	240 - 275	°C
Adapter Temperature	240 - 275	°C
Die Temperature	240 - 275	°C
Waterbath Temperature	25 - 35	°C

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	>4.E+16	Ω.cm	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	1602	J/m	ASTM D4812
Izod Impact, notched, 23°C	53	J/m	ASTM D256
Modified Gardner, 23°C	40	J	ASTM D3029

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	51	MPa	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	300	%	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	82	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2340	MPa	ASTM D790
Hardness, Rockwell R	117	-	ASTM D785

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.31	-	ASTM D792
Specific Volume	0.76	cm³/g	ASTM D792
Water Absorption, (23°C/24hrs)	0.08	%	ASTM D570
Mold Shrinkage, flow, 0.75-2.3 mm	0.9 - 1.6	%	SABIC method
Mold Shrinkage, flow, 2.3-4.6 mm	1.5 - 2.3	%	SABIC method
Mold Shrinkage, xflow, 0.75-2.3 mm	1 - 1.7	%	SABIC method
Mold Shrinkage, xflow, 2.3-4.6 mm	1.6 - 2.4	%	SABIC method
Melt Volume Rate, MVR at 250°C/2.16 kg	9	cm³/10 min	ASTM D1238
Melt Volume Rate, MVR at 250°C/2.16 kg	9	cm³/10 min	ISO 1133

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 6.4 mm, unannealed	154	°C	ASTM D648
HDT, 1.82 MPa, 6.4 mm, unannealed	54	°C	ASTM D648
CTE, -40°C to 40°C, flow	8.1E-05	1/°C	ASTM E831
CTE, 60°C to 138°C, flow	1.4E-04	1/°C	ASTM E831

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES