LNP™ COLORCOMP™ Compound WX09915

LNP COLORCOMP WX09915 compound is based on Polybutylene Terephthalate (PBT) resin. Added features of this grade include: Flame Retardant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate + PBT (PC+PBT)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Aesthetics/Visual effects
Flame Retardant
No PFAS intentionally added

Industry

Material previously used in

Automotive Interiors
Commercial Appliance
Home Appliances
Home Decoration
Mobile Phone - Computer - Tablets
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Under the hood

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	39	J/m	ASTM D256
Izod Impact, unnotched, 23°C	1450	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	5.4	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	86.7	kJ/m²	ISO 180/1U
Multiaxial Impact	50.8	J	ASTM D3763
Multiaxial Impact	38.6	J	ISO 6603

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	121	°C
Drying Time (Cumulative)	4	Hrs
Melt Temperature	237 - 265	°C
Front - Zone 3 Temperature	260 - 271	°C
Middle - Zone 2 Temperature	243 - 254	°C
Rear - Zone 1 Temperature	221 - 232	°C
Mold Temperature	82 - 98	°C
Back Pressure	0.17 - 0.34	MPa
Screw Speed	30 - 60	rpm
Maximum Moisture Content	0.05	%

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 5 mm/min	2694	MPa	ASTM D638
Tensile Stress, yld, Type I, 5 mm/min	54	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	49	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	7	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	16	%	ASTM D638
Tensile Modulus, 1 mm/min	2721	MPa	ISO 527
Tensile Stress, yield, 5 mm/min	53	MPa	ISO 527
Tensile Stress, break, 5 mm/min	48	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	6.9	%	ISO 527
Tensile Strain, break, 5 mm/min	14.8	%	ISO 527
Flexural Modulus, 1.3 mm/min, 50 mm span	2640	MPa	ASTM D790
Flexural Modulus, 2 mm/min	2619	MPa	ISO 178
Flexural Stress	88	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.36	g/cm³	ASTM D792
Specific Gravity	1.36	-	ASTM D792
Mold Shrinkage, flow, 24 hrs	2.3	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	2.4	%	ASTM D955
Moisture Absorption, (23°C/50% RH/24 hrs)	0.58	%	ASTM D570
Moisture Absorption (23°C / 50% RH)	0.05	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	65	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	155	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	68	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	143	°C	ISO 75/Bf
CTE, -30°C to 30°C, flow	9E-5	1/°C	ASTM D696
CTE, -30°C to 30°C, xflow	9E-5	1/°C	ASTM D696

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES