LNP ELCRES CRX9411W is an amorphous Polycarbonate (PC) copolymer resin that offers medium flow, UL V0 rating @ 1.6 mm for all colors, and high ductility in combination with excellent chemical resistance. This grade is available for custom coloring and is intended for a wide variety of healthcare applications that need improved chemical resistance. This grade is subjected to SABIC healthcare management of change policy and formulation lock.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Dielectric Constant | |||
| – 100 MHz | 2.82 | - | SABIC method |
| – 2.47 GHz | 2.78 | - | SABIC method |
| Dissipation Factor | |||
| – 100 MHz | 0.0066 | - | SABIC method |
| – 2.47 GHz | 0.0053 | - | SABIC method |
| Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 0 | ≥0.8 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥0.8 | mm | UL 746A |
| Surface Resistivity | >1.E+13 | Ω | ASTM D257 |
| Volume Resistivity | >1.E+15 | Ω.cm | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94V-0 Flame Class Rating | 1.6 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 765 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 680 | J/m | ASTM D256 |
| Izod Impact, notched, -60°C | 609 | J/m | ASTM D256 |
| Izod Impact, notched, -70°C | 570 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | NB | J/m | ASTM D4812 |
| Izod Impact, unnotched, -70°C | NB | J/m | ASTM D4812 |
| Instrumented Dart Impact Ductility, 23°C | 100 | % | ASTM D3763 |
| Instrumented Dart Impact Total Energy, 23°C | 61 | J | ASTM D3763 |
| Izod Impact, notched 80*10*3 +23°C | 55 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -70°C | 35 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*3 -70°C | NB | kJ/m² | ISO 180/1U |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 65 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -70°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 12 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 290 - 340 | °C | |
| Rear - Zone 1 Temperature | 270 - 320 | °C | |
| Middle - Zone 2 Temperature | 280 - 330 | °C | |
| Front - Zone 3 Temperature | 290 - 340 | °C | |
| Nozzle Temperature | 290 - 340 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Shot to Cylinder Size | 40 - 80 | % | |
| Vent Depth | 0.025 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 50 mm/min | 52 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 59 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | >100 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 1920 | MPa | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2000 | MPa | ASTM D790 |
| Flexural Strength, 1.3 mm/min, 50 mm span | 85 | MPa | ASTM D790 |
| Tensile Stress, yield, 50 mm/min | 50 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 57 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | >100 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1858 | MPa | ISO 527 |
| Flexural Strength, 2 mm/min | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2012 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.2 | - | ASTM D792 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 9.5 | cm³/10 min | ASTM D1238 |
| Melt Flow Rate, 300°C/1.2 kgf | 10 | g/10 min | ASTM D1238 |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Moisture Absorption, (23°C/50% RH/24hrs) | 0.08 | % | ISO 62-4 |
| Water Absorption, (23°C/24hrs) | 0.3 | % | ISO 62-1 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 9 | cm³/10 min | ISO 1133 |
| Mold Shrinkage, flow | 0.4 - 0.9 | % | SABIC method |
| Mold Shrinkage, xflow | 0.4 - 0.9 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 125 | °C | ASTM D648 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 138 | °C | ASTM D648 |
| Vicat Softening Temp, Rate B/50 | 142 | °C | ASTM D1525 |
| Vicat Softening Temp, Rate B/120 | 146 | °C | ASTM D1525 |
| CTE, -40°C to 40°C, flow | 7E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 7E-05 | 1/°C | ASTM E831 |
| Ball Pressure Test, 125°C +/- 2°C | PASS | - | IEC 60695-10-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 123 | °C | ISO 75/Af |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 137 | °C | ISO 75/Bf |
| Vicat Softening Temp, Rate B/50 | 142 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 144 | °C | ISO 306 |
| CTE, -40°C to 40°C, flow | 7E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7E-05 | 1/°C | ISO 11359-2 |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.