LNP ELCRES CX7410 Polycarbonate (PC)/Acrylonitrile Butadiene Styrene (ABS)/PC siloxane copolymer (PC/ABS/EXL) blend is an injection moldable, medium flow, non chlorinated/brominated flame retardant grade. The product is available in a wide range of opaque colors and has a UL94 V0 at 1.5mm and 5VB at 2mm flame rating. This grade has improved chemical resistance, ductility and heat properties compared to standard PC/ABS blends.
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Recognized, 94V-0 Flame Class Rating | 1.5 | mm | UL 94 |
| UL Recognized, 94-5VB Flame Class Rating | ≥2 | mm | UL 94 |
| Glow Wire Ignitability Temperature, 3.0 mm | 875 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 1.0 mm | 960 | °C | IEC 60695-2-13 |
| UL Yellow Card Link | View | - | - |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact | |||
| – Izod Impact, notched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1A |
| – Izod Impact, notched 80*10*4 0°C | 17 | kJ/m² | ISO 180/1A |
| – Izod Impact, notched 80*10*4 -30°C | 15 | kJ/m² | ISO 180/1A |
| – Izod Impact, notched 80*10*3 +23°C | 54 | kJ/m² | ISO 180/1A |
| – Izod Impact, notched 80*10*3 +10°C | 30 | kJ/m² | ISO 180/1A |
| – Izod Impact, notched 80*10*3 0°C | 16 | kJ/m² | ISO 180/1A |
| – Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| – Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| – Izod Impact, notched, 23°C | 700 | J/m | ASTM D256 |
| – Izod Impact, notched, 10°C | 600 | J/m | ASTM D256 |
| – Izod Impact, notched, 0°C | 140 | J/m | ASTM D256 |
| – Izod Impact, notched, -30°C | 120 | J/m | ASTM D256 |
| – Izod Impact, unnotched, 23°C | NB | J/m | ASTM D4812 |
| Charpy | |||
| – Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 46 | kJ/m² | ISO 179/1eA |
| – Charpy 0°C, V-notch Edgew 80*10*4 sp=62mm | 14 | kJ/m² | ISO 179/1eA |
| – Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 65 | kJ/m² | ISO 179/1eA |
| – Charpy 10°C, V-notch Edgew 80*10*3 sp=62mm | 52 | kJ/m² | ISO 179/1eA |
| – Charpy 0°C, V-notch Edgew 80*10*3 sp=62mm | 18 | kJ/m² | ISO 179/1eA |
| – Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 85 - 95 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.04 | % | |
| Hopper Temperature | 40 - 60 | °C | |
| Melt Temperature | 265 - 290 | °C | |
| Rear - Zone 1 Temperature | 245 - 270 | °C | |
| Middle - Zone 2 Temperature | 255 - 280 | °C | |
| Front - Zone 3 Temperature | 265 - 290 | °C | |
| Nozzle Temperature | 265 - 290 | °C | |
| Mold Temperature | 65 - 85 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Shot to Cylinder Size | 30 - 80 | % | |
| Vent Depth | 0.038 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Modulus, 1 mm/min | 2500 | MPa | ISO 527 |
| Tensile Stress, yield, 50 mm/min | 65 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 53 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4.6 | % | ISO 527 |
| Tensile Nominal Strain, break, 50 mm/min | 40 | % | ISO 527 |
| Flexural Modulus, 2 mm/min | 2600 | MPa | ISO 178 |
| Flexural Strength, 2 mm/min | 98 | MPa | ISO 178 |
| Flexural Stress at 3.5% strain, 2 mm/min | 81 | MPa | ISO 178 |
| Tensile Modulus, 50 mm/min | 2550 | MPa | ASTM D638 |
| Tensile Stress, yld, Type I, 50 mm/min | 65 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 55 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4.6 | % | ASTM D638 |
| Tensile Nominal Strain, brk, Type I, 50 mm/min | 60 | % | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2600 | MPa | ASTM D790 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 100 | MPa | ASTM D790 |
| Flexural Stress at 5% strain, 1.3 mm/min, 50 mm span | 100 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.2 | g/cm³ | ISO 1183 |
| Moisture Absorption, (23°C/50% RH/24hrs) | 0.12 | % | ISO 62-4 |
| Water Absorption, (23°C/saturated) | 0.24 | % | ISO 62-1 |
| Mold Shrinkage, flow | 0.28 | % | SABIC method |
| Mold Shrinkage, xflow | 0.33 | % | SABIC method |
| Melt Volume Rate, MVR at 260°C/2.16 kg | 10 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 29 | cm³/10 min | ISO 1133 |
| Specific Gravity | 1.2 | - | ASTM D792 |
| Water Absorption, (23°C/Saturated) | 0.24 | % | ASTM D570 |
| Water Absorption, (23°C/24hrs) | 0.12 | % | ASTM D570 |
| Melt Flow Rate, 260°C/2.16 kgf | 11 | g/10 min | ASTM D1238 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE | |||
| – CTE, -40°C to 80°C, flow | 69.1 | µm/(m-°C) | ISO 11359-2 |
| – CTE, -40°C to 80°C, xflow | 71.6 | µm/(m-°C) | ISO 11359-2 |
| – CTE, -40°C to 80°C, flow | 69.1 | µm/(m-°C) | ASTM E831 |
| – CTE, -40°C to 80°C, xflow | 71.6 | µm/(m-°C) | ASTM E831 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 98 | °C | ISO 75/Af |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 108 | °C | ISO 75/Bf |
| Vicat Softening Temp, Rate B/50 | 113 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 114 | °C | ISO 306 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 95 | °C | ASTM D648 |
| Vicat Softening Temp, Rate B/50 | 113 | °C | ASTM D1525 |
| Vicat Softening Temp, Rate B/120 | 114 | °C | ASTM D1525 |
| Ball Pressure Test, 75°C +/- 2°C | PASS | - | IEC 60695-10-2 |
| Relative Temp Index, Elec | 90 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 90 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 90 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.