LNP™ ELCRES™ CXL1521F5

LNP ELCRES CXL1521F5 is a glass reinforced Polycarbonate (PC) copolymer/Polybutylene Terephthalate (PBT) blends. This compound offers high modulus and balanced ductility in combination with excellent chemical resistance.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate + PBT (PC+PBT)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Chemical Resistance
High Flow
High stiffness/Strength
Impact resistant

Industry

Material previously used in

Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Mobile Phone

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod impact, notched
– -20°C	120	J/m	ASTM D256
– 23°C	180	J/m	ASTM D256
– 80104 +23°C	15	kJ/m²	ISO 180/1A
Izod Impact, Unnotched
– 23°C	840	kJ/m²	ASTM D4812
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	17	kJ/m²	ISO 179/1eA

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110 - 120	°C
Drying Time	3 - 4	Hrs
Melt Temperature	250 - 275	°C
Nozzle Temperature	245 - 275	°C
Front - Zone 3 Temperature	250 - 270	°C
Middle - Zone 2 Temperature	250 - 270	°C
Rear - Zone 1 Temperature	240 - 260	°C
Mold Temperature	50 - 100	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	95	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	3.2	%	ASTM D638
Tensile Modulus, 5 mm/min	6900	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	150	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	6000	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	95	MPa	ISO 527
Tensile Strain, break, 5 mm/min	3.2	%	ISO 527
Tensile Modulus, 1 mm/min	6800	MPa	ISO 527
Flexural Strength, 2 mm/min	150	MPa	ISO 178
Flexural Modulus, 2 mm/min	5900	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.42	-	ASTM D792
Density	1.42	g/cm³	ISO 1183
Melt Volume Rate, MVR at 260°C/5.0 kg	14	cm³/10 min	ISO 1133
Mold Shrinkage, flow	0.1 - 0.3	%	SABIC method
Mold Shrinkage, xflow	0.3 - 0.5	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	180	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	214	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	177	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	212	°C	ISO 75/Bf

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES