LNP™ ELCRES™ EXL1414AML

ELCRES EXL1414AML is a polycarbonate (PC) siloxane copolymer resin containing antimicrobial additives, medium flow, opaque and injection molding (IM) grade. This resin offers extreme low temperature (-40 degrees) ductility in combination with excellent processability and release with opportunities for shorter IM cycle times compared with standard PC.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Impact resistant
Low temperature impact
No PFAS intentionally added

Industry

Material previously used in

Automotive Exteriors
Automotive Interiors
Automotive Under the Hood
Building Component
Commercial Appliance
Defense
Electrical
General Healthcare
Home Appliances
Lighting
Mobile Phone - Computer - Tablets
Ophthalmics
Patient Testing
Personal Accessory
Personal Recreation
Recreational/Specialty Vehicles
Sport/Leisure
Surgical devices
Water Management

Applications

Possible usage of material

Air Conditioning
Audio
Auto Aftermarket
Body Protection
Circuit Protection
Cooking Range
Data Management
Data Transfer
Displays
Document Handling
Electronic Components
Electronics
Enclosure/Housing/Cover
Enclosures
EV Infrastructure
Eyeglasses
Fuel Handling
Furnace/Heater
Head Protection
Heavy Vehicles
Infotainment/Telematic
Lab Ware and Clinical Diagnostics
Lawn/Garden
LED Lighting
Medical Device
Medical Facility Infrastructure
Monitoring and Imaging
Motorcycle
Non-LED Lighting
Personal Care
Personal Computing
Photo/Video Camera
Photovoltaic Components
Power Manangement
Refrigerator
Small Appliance
Smart/ID Card
Surgical Tray
Travel Suitcase
Vacuum Cleaner
Vending Machine
Watch/Jewelry
Water Treatment/Filtration
Wearables
Wireless Communications
Wiring Devices
Irrigation

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	890	J/m	ASTM D256
Izod Impact, notched, -30°C	700	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	70	J	ASTM D3763
*Izod Impact, notched 80103 +23°C*	70	kJ/m²	ISO 180/1A
*Izod Impact, notched 80103 -30°C*	52	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80103 +23°C*	NB	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80103 -30°C*	NB	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80103 sp=62mm*	72	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80103 sp=62mm*	49	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80103 sp=62mm*	NB	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80103 sp=62mm*	NB	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	3 - 4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	295 - 315	°C
Nozzle Temperature	290 - 310	°C
Front - Zone 3 Temperature	295 - 315	°C
Middle - Zone 2 Temperature	280 - 305	°C
Rear - Zone 1 Temperature	270 - 295	°C
Mold Temperature	70 - 95	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	54	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	64	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	5	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	115	%	ASTM D638
Tensile Modulus, 50 mm/min	2085	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	86	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2100	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	53	MPa	ISO 527
Tensile Stress, break, 50 mm/min	64	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	6	%	ISO 527
Tensile Strain, break, 50 mm/min	119	%	ISO 527
Tensile Modulus, 1 mm/min	2066	MPa	ISO 527
Flexural Strength, 2 mm/min	73	MPa	ISO 178
Flexural Modulus, 2 mm/min	2223	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.19	-	ASTM D792
Mold Shrinkage, flow, 3.2 mm	0.4 - 0.8	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	0.4 - 0.8	%	SABIC method
Melt Flow Rate, 300°C/1.2 kgf	11	g/10 min	ASTM D1238
Density	1.19	g/cm³	ISO 1183
Water Absorption, (23°C/saturated)	0.35	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)	0.15	%	ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg	10	cm³/10 min	ISO 1133

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	139	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	125	°C	ASTM D648
*HDT/Be, 0.45MPa Edgew 120104 sp=100mm*	140	°C	ISO 75/Be
*HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm*	128	°C	ISO 75/Ae
CTE, -40°C to 40°C, flow	7.0E-5	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	7.47E-5	1/°C	ASTM E831
CTE, 23°C to 80°C, flow	7.2E-5	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	7.2E-5	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	140	°C	ASTM D1525
Vicat Softening Temp, Rate B/50	140	°C	ISO 306
Vicat Softening Temp, Rate B/120	139	°C	ISO 306
Ball Pressure Test, 125°C +/- 2°C	Passes	-	IEC 60695-10-2

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES