LNP ELCRES FST2432 resin is a medium flow, UV stabilized, glass fiber reinforced polycarbonate Copolymer Resin for injection molding in opaque colors. This non-chlorinated, non-brominated flame retardant resin is EN 45545 R6–HL2 compliant and an ideal candidate for train seating applications.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Smoke density, DS-4, 50 kW/m2 | <300 | - | ISO 5659-2 |
| Smoke density, VOF4, 50 kW/m2 | <600 | - | ISO 5659-2 |
| Smoke toxicity, CITG (8 min), 50 kW/m2 | <0.9 | - | ISO 5659-2 |
| Heat release, MAHRE, 50 kW/m2 | <90 | kW/m² | ISO 5660-1 |
| Fire Safety Hazard Level - Requirement set R6 | HL2 | - | EN 45545-2 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 17 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 10 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | 86 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 68 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*3 +23°C | 16 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 9 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*3 +23°C | 91 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*3 -30°C | 69 | kJ/m² | ISO 180/1U |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 15 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | 96 | kJ/m² | ISO 179/1eU |
| Izod Impact, notched, 23°C | 143 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | 1200 | J/m | ASTM D4812 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 105 - 110 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Hopper Temperature | 40 - 60 | °C | |
| Maximum Moisture Content | 0.04 | % | |
| Melt Temperature | 285 - 320 | °C | |
| Rear - Zone 1 Temperature | 265 - 300 | °C | |
| Middle - Zone 2 Temperature | 275 - 310 | °C | |
| Front - Zone 3 Temperature | 285 - 320 | °C | |
| Mold Temperature | 85 - 120 | °C | |
| Back Pressure | 0.2 - 0.7 | MPa | |
| Screw Speed | 30 - 80 | rpm | |
| Vent Depth | 0.038 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Modulus, 1 mm/min | 3850 | MPa | ISO 527 |
| Tensile Stress, yield, 5 mm/min | 50 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 42 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3.6 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 7 | % | ISO 527 |
| Flexural Modulus, 2 mm/min | 3800 | MPa | ISO 178 |
| Flexural Strength, 2 mm/min | 83 | MPa | ISO 178 |
| Tensile Modulus, 5 mm/min | 3900 | MPa | ASTM D638 |
| Tensile Stress, yld, Type I, 5 mm/min | 50 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 41 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3.8 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 6.8 | % | ASTM D638 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.29 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 12 | cm³/10 min | ISO 1133 |
| Moisture Absorption, (23°C/50% RH/Equilibrium) | 0.12 | % | ISO 62-4 |
| Mold Shrinkage, flow | 0.3 - 0.4 | % | SABIC method |
| Mold Shrinkage, xflow | 0.35 - 0.45 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 118 | °C | ISO 75/Af |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 126 | °C | ISO 75/Bf |
| Vicat Softening Temp, Rate B/50 | 124 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 126 | °C | ISO 306 |
| CTE, -40°C to 90°C, flow | 3.6E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 90°C, xflow | 7.4E-05 | 1/°C | ISO 11359-2 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 116 | °C | ASTM D648 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 125 | °C | ASTM D648 |
| Ball Pressure Test, 125°C +/- 2°C | PASS | - | IEC 60695-10-2 |