LNP ELCRES FST2733E is a glass fiber reinforced Polycarbonate Copolymer Resin for sheet extrusion and part production by thermoforming processes. This UV stabilized, non-Br/Cl flame retardant resin with no intentionally-added PFAS, is intended for train interior applications requiring EN 45545 R1–HL3 compliant materials (e.g. side panels & partition walls). Available in opaque colors.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Smoke density, DS-4, 50 kW/m2 | <150 | - | ISO 5659-2 |
| Smoke density, VOF4, 50 kW/m2 | <300 | - | ISO 5659-2 |
| Smoke toxicity, CITG (8 min), 50 kW/m2 | <0.75 | - | ISO 5659-2 |
| Heat release, MAHRE, 50 kW/m2 | <60 | kW/m² | ISO 5660-1 |
| Lateral Flame Spread, CFE | >20 | kW/m² | ISO 5658-2 |
| Fire Safety Hazard Level - Requirement set R1 | HL3 | - | EN 45545-2 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | 120 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*3 +23°C | 7 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 5 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*3 +23°C | 105 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*3 -30°C | 105 | kJ/m² | ISO 180/1U |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 7 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | 75 | kJ/m² | ISO 179/1eU |
| Izod Impact, notched, 23°C | 78 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | 975 | J/m | ASTM D4812 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Modulus, 1 mm/min | 5750 | MPa | ISO 527 |
| Tensile Stress, yield, 5 mm/min | 60 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 48 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 5 | % | ISO 527 |
| Tensile Nominal Strain, break, 5 mm/min | 8 | % | ISO 527 |
| Flexural Modulus, 2 mm/min | 5800 | MPa | ISO 178 |
| Flexural Strength, 2 mm/min | 109 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 9 | % | ISO 178 |
| Flexural Stress at 3.5% strain, 2 mm/min | 97 | MPa | ISO 178 |
| Tensile Modulus, 5 mm/min | 5650 | MPa | ASTM D638 |
| Tensile Stress, yld, Type I, 5 mm/min | 61 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 48 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 5 | % | ASTM D638 |
| Tensile Nominal Strain, brk, Type I, 5 mm/min | 8 | % | ASTM D638 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 5.5 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 260°C/2.16 kg | 2 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 5.5 | cm³/10 min | ISO 1133 |
| Moisture Absorption (23°C / 50% RH) | 0.05 | % | ISO 62 |
| Specific Gravity | 1.47 | - | ASTM D792 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 90 - 110 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 18 | Hrs | |
| Maximum Moisture Content | 0.05 | % | |
| Melt Temperature | 210 - 250 | °C | |
| Barrel - Zone 1 Temperature | 180 - 210 | °C | |
| Barrel - Zone 2 Temperature | 200 - 230 | °C | |
| Barrel - Zone 3 Temperature | 210 - 250 | °C | |
| Barrel - Zone 4 Temperature | 210 - 250 | °C | |
| Die Temperature | 210 - 250 | °C | |
| Roll Stack Temp - Bottom | 90 - 120 | °C | |
| Roll Stack Temp - Middle | 90 - 120 | °C | |
| Roll Stack Temp - Top | 90 - 120 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 105 | °C | ISO 75/Af |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 114 | °C | ISO 75/Bf |
| Vicat Softening Temp, Rate B/50 | 115 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 116 | °C | ISO 306 |
| CTE, -40°C to 90°C, flow | 2.8E-5 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 90°C, xflow | 7.0E-5 | 1/°C | ISO 11359-2 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 104 | °C | ASTM D648 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 113 | °C | ASTM D648 |
| Ball Pressure Test, 75°C +/- 2°C | PASS | - | IEC 60695-10-2 |