LNP™ ELCRES™ FXD9111T

LNP ELCRES FXD9111T is a PC-Siloxane copolymer resin with light diffusion special effects, which is part of the VISUALFX product family. Color package may affect performance. Added features of this grade include: Transparent/translucent, non-chlorinated, non-brominated flame retardant. FR V0 at 2mm.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Aesthetics/Visual effects
No PFAS intentionally added
Non Cl/Br flame retardant
Transparent/Translucent

Industry

Material previously used in

Commercial Appliance
Electrical
Home Appliances
Lighting
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Mobile Phone
Lighting

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	2	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	643	J/m	ASTM D256
Izod Impact, unnotched, 23°C	2140	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	52	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	182	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	55	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	131	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	90	°C
Drying Time	3 - 4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	250 - 285	°C
Nozzle Temperature	250 - 285	°C
Front - Zone 3 Temperature	250 - 285	°C
Middle - Zone 2 Temperature	250 - 285	°C
Rear - Zone 1 Temperature	250 - 285	°C
Mold Temperature	59 - 90	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	59	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	57	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	6	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	97	%	ASTM D638
Tensile Modulus, 50 mm/min	2318	MPa	ASTM D638
Flexural Stress at 5% strain, 1.3 mm/min, 50 mm span	88	MPa	ASTM D790
Flexural Strength, 1.3 mm/min, 50 mm span	94	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2230	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	58	MPa	ISO 527
Tensile Stress, break, 50 mm/min	51	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5	%	ISO 527
Tensile Strain, break, 50 mm/min	71	%	ISO 527
Tensile Modulus, 1 mm/min	2297	MPa	ISO 527
Flexural Stress at 3.5% strain, 2 mm/min	86.3	MPa	ISO 178
Flexural Strain, break, 2 mm/min	7.6	%	ISO 178
Flexural Strength, 2 mm/min	87.9	MPa	ISO 178
Flexural Modulus, 2 mm/min	2085	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.2	-	ASTM D792
Density	1.197	g/cm³	ISO 1183
Water Absorption, (23°C/24hrs)	0.1	%	ISO 62-1
Moisture Absorption, (23°C/50% RH/24hrs)	0.03	%	ISO 62-4
Melt Flow Rate, 300°C/1.2 kgf	19.4	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 300°C/1.2 kg	18.4	cm³/10 min	ASTM D1238
Mold Shrinkage, flow	0.63	%	SABIC method
Mold Shrinkage, xflow	0.69	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	119	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	109	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	118	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	106	°C	ISO 75/Af
CTE, -40°C to 95°C, flow	7.9E-05	1/°C	ASTM E831
CTE, -40°C to 95°C, xflow	8.5E-05	1/°C	ASTM E831
CTE, 23°C to 80°C, flow	8.2E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	8.6E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate A/50	131	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	125	°C	ASTM D1525
Vicat Softening Temp, Rate B/50	124	°C	ISO 306
Vicat Softening Temp, Rate B/120	125	°C	ISO 306
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES