LNP™ ELCRES™ FXE9111T

ELCRES FXE9111T PC-Siloxane copolymer resin is an injection molding grade. Non-chlorinated, non-brominated flame retardant with FR V0 at 2mm. This resin offers good low temperature ductility in combination with high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. Available for VISUALFX capability in “Illuminate” colors. ELCRES FXE9111T resin may be an excellent candidate for a broad range of applications, including but not limited to Automobile, Appliance, Electronics, etc.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Aesthetics/Visual effects
Enhanced mold release
Flame Retardant
Good Processability
Impact resistant
Low temperature impact
No PFAS intentionally added
Non Cl/Br flame retardant

Industry

Material previously used in

Automotive Interiors
Commercial Appliance
Home Appliances
Home Decoration
Industrial Packaging
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Building/Construction Sheet
Commercial Appliance
Enclosure/Housing/Cover
Interior
Lighting
Small Appliance
Toy

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	≥2.0	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	2150	J/m	ASTM D4812
Izod Impact, notched, 10°C	500	J/m	ASTM D256
Izod Impact, notched, 23°C	777	J/m	ASTM D256
*Izod Impact, notched 80104 +23°C*	57	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	180	kJ/m²	ISO 180/1U
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	130	kJ/m²	ISO 179/1eU
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	59	kJ/m²	ISO 179/1eA

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	90	°C
Drying Time	3 - 4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	250 - 285	°C
Nozzle Temperature	250 - 285	°C
Front - Zone 3 Temperature	250 - 285	°C
Middle - Zone 2 Temperature	250 - 285	°C
Rear - Zone 1 Temperature	250 - 285	°C
Mold Temperature	50 - 90	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	57	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	54	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	5	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	92	%	ASTM D638
Tensile Modulus, 50 mm/min	2190	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	90	MPa	ASTM D790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	89	MPa	ASTM D790
Flexural Stress at 5% strain, 1.3 mm/min, 50 mm span	85	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2180	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	58	MPa	ISO 527
Tensile Stress, break, 50 mm/min	52	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5	%	ISO 527
Tensile Strain, break, 50 mm/min	95	%	ISO 527
Tensile Modulus, 1 mm/min	2230	MPa	ISO 527
Flexural Stress at 3.5% strain, 2 mm/min	67.4	MPa	ISO 178
Flexural Strain, break, 2 mm/min	7.5	%	ISO 178
Flexural Strength, 2 mm/min	86.6	MPa	ISO 178
Flexural Modulus, 2 mm/min	2190	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.20	-	ASTM D792
Density	1.201	g/cm³	ISO 1183
Water Absorption, (23°C/24hrs)	0.11	%	ISO 62-1
Moisture Absorption, (23°C/50% RH/24hrs)	0.04	%	ISO 62-4
Melt Flow Rate, 300°C/1.2 kgf	19.5	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 300°C/1.2 kg	18.3	cm³/10 min	ASTM D1238
Mold Shrinkage, flow	0.66	%	SABIC method
Mold Shrinkage, xflow	0.73	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	119	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	107	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	119	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	107	°C	ISO 75/Af
CTE, -40°C to 95°C, flow	7.5E-05	1/°C	ASTM E831
CTE, -40°C to 95°C, xflow	8.3E-05	1/°C	ASTM E831
CTE, 23°C to 80°C, flow	8.1E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	8.6E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate A/50	132	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	126	°C	ASTM D1525
Vicat Softening Temp, Rate B/50	125	°C	ISO 306
Vicat Softening Temp, Rate B/120	126	°C	ISO 306
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience