LNP ELCRES FXM1838 is based on Polycarbonate (PC) copolymer resin with excellent flowability, UV stabilized in special metallic colors (color package may affect certain properties). It is targeted for applications like mobility exteriors, trims or other adjacent pain-free applications.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 112 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | NB | J/m | ASTM D4812 |
| Izod Impact, notched 80*10*3 +23°C | 8 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact Total Energy, 23°C | 57.5 | J | ASTM D3763 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 105 - 110 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Hopper Temperature | 50 - 80 | °C | |
| Melt Temperature | 260 - 305 | °C | |
| Nozzle Temperature | 255 - 300 | °C | |
| Front - Zone 3 Temperature | 260 - 305 | °C | |
| Middle - Zone 2 Temperature | 250 - 295 | °C | |
| Rear - Zone 1 Temperature | 240 - 280 | °C | |
| Mold Temperature | 80 - 110 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 50 mm/min | 53 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 54 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 84 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2242 | MPa | ASTM D638 |
| Flexural Strength, 1.3 mm/min, 50 mm span | 93 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2162 | MPa | ASTM D790 |
| Tensile Stress, yield, 50 mm/min | 58 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 59 | MPa | ISO 527 |
| Tensile Strain, break, 50 mm/min | 90 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2240 | MPa | ISO 527 |
| Flexural Strength, 2 mm/min | 92 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2228 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.19 | - | ASTM D792 |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Flow Rate, 300°C/1.2 kgf | 39 | g/10 min | ASTM D1238 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 40 | cm³/10 min | ISO 1133 |
| Mold Shrinkage, flow | 0.2 - 0.7 | % | SABIC method |
| Mold Shrinkage, xflow | 0.2 - 0.7 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 108 | °C | ASTM D648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 111 | °C | ISO 75/Af |
| CTE | |||
| – -30°C to 85°C, flow | 6.9E-5 | 1/°C | ISO 11359-2 |
| – -30°C to 85°C, xflow | 6.9E-5 | 1/°C | ISO 11359-2 |